Structure and Properties of Mg-Ni-Fe Based Nanaocomposite Prepared by Spark Synthesis

SYSNO ASEP	0177623
Druh ASEP	C - Konferenční příspěvek (mezinárodní konf.)
Zařazení RIV	D - Článek ve sborníku
Název	Structure and Properties of Mg-Ni-Fe Based Nanaocomposite Prepared by Spark Synthesis
Tvůrce(i)	Schneeweiss, Oldřich (UFM-A)_{RID, ORCID} Jirásková, Yvonna (UFM-A)_{RID, ORCID} Žák, Tomáš (UFM-A)_RID Bezdička, Petr (UACH-T)_{SAI, RID, ORCID} Večerníková, Eva (UACH-T)_SAI
Zdroj.dok.	SMARTON 5 Workshop: Functional Surfaces and Materials. Exploring the Vectorial World. - Nijmegen : Katholieke Universiteit Nijmegen, 2001
Rozsah stran	s. 48
Poč.str.	1 s.
Akce	SMARTON Workshop: Functional Surfaces and Materials. Exploring the Vectorial World /5./
Datum konání	15.11.2001-18.11.2001
Místo konání	Maatsricht
Země	NL - Nizozemsko
Typ akce	WRD
Jazyk dok.	eng - angličtina
Země vyd.	NL - Nizozemsko
Klíč. slova	nanomaterials ; magnetic properties ; Mössbauer spectroscopy
Vědní obor RIV	BM - Fyzika pevných látek a magnetismus
CEP	GV202/98/K002 GA ČR - Grantová agentura ČR
	GA202/01/0668 GA ČR - Grantová agentura ČR
	ME 209 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy
	KSK1010104 GA AV ČR - Akademie věd
CEZ	AV0Z2041904 - UFM-A
Anotace	A composite based on 3d metals particles embedded in MgO matrix is a promising material for application in sensors using high magnetoresistance. We prepared Mg-Fe-Ni nanocomposite using spark synthesis of the pure Mg, and permalloy (Ni3Fe) electrodes. The magnetic separation and sedimentation treatments were used for separation of nanocrystalline parts from the as-prepared powders. In the as-prepared powder, a-Fe + g-Ni3Fe, Fe(Ni) in Mg, and FeO phases were determined using the Mössbauer phase analysis. Some of the phases were confirmed by the x-ray diffraction measurements. The TG/DTA results indicate presence nanoparticles of Fe-Ni hydrides and high adsorption capacity of moisture and air gases. Temperature dependence of magnetization shows spin-glass like behaviour of the sample. Transformation of the Fe(Ni) in Mg phase and the hydride phases into a-Fe + g Ni3Fe and simultaneously an increasing in FeO + MgO were observed after annealing in vacuum (10-3 Pa) or in the protective atmosphere (H2).