RBS, XPS and AFM Study of Ag Thin Films and Polyethylene Foils Interface Modified by Plasma Treatment
- 1.
SYSNO ASEP 0080058 Druh ASEP G - Konferenční sborník (mezinárodní konf.) Zařazení RIV Není vybrán druh dokumentu Název RBS, XPS and AFM Study of Ag Thin Films and Polyethylene Foils Interface Modified by Plasma Treatment Překlad názvu Studium rozhraní polyetylénových fólií s Ag tenkou vrstvou plasmaticky modifikovaných metodami RBS, XPS a AFM Tvůrce(i) Macková, Anna (UJF-V) RID, ORCID, SAI
Švorčík, V. (CZ)
Strýhal, Z. (CZ)
Pavlík, J. (CZ)
Malinský, Petr (UJF-V) RID, ORCID, SAIVyd. údaje Bratislava: Comenius University, 2007 ISBN 978-80-89186-13-6 Poč.str. 2 s. Akce 16th Symposium on Application of Plasma Processes Datum konání 20.01.2007-25.01.2007 Místo konání Podbánske Země SK - Slovensko Typ akce WRD Jazyk dok. eng - angličtina Země vyd. SK - Slovensko Klíč. slova metallized polymers ; RBS ; plasma modification Vědní obor RIV BG - Jaderná, atomová a mol. fyzika, urychlovače CEP LC06041 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy CEZ AV0Z10480505 - UJF-V (2005-2011) Anotace The mechanical and electric properties of the metal-polymer interface are strongly affected by the degree of metal-polymer diffusion and intermixing. We performed a study of the diffusion of the Ag atoms in polyethylene (LDPE and HDPE). Thin Ag layers were deposited using a diode-sputtering technique on polymer foils at room temperature. Simultaneous post-deposition annealing and plasma treatment were used to induce metal-polymer intermixing. Rutherford Backscattering Spectrometry (RBS), X-ray Photoelectron Spectroscopy (XPS)and Atomic Force Microscopy (AFM) were used to determine the integral amount of metal, the metal chemical structure in the surface layer and the metal layer morphology changes. Ag thin films exhibit dramatic changes of the chemical composition and surface morphology after Ar plasma treatment. The metal mobility is strongly influenced by the temperature, which was close to the melting point of used polymers. Ag cluster diffusion should be expected in this case. Pracoviště Ústav jaderné fyziky Kontakt Markéta Sommerová, sommerova@ujf.cas.cz, Tel.: 266 173 228 Rok sběru 2007
Počet záznamů: 1