Dislocation arrangements in cyclically strained Inconel 713 LC
- 1.
SYSNO ASEP 0047301 Druh ASEP A - Abstrakt Zařazení RIV Záznam nebyl označen do RIV Zařazení RIV Není vybrán druh dokumentu Název Dislocation arrangements in cyclically strained Inconel 713 LC Překlad názvu Dislokační uspořádání cyklicky deformovaného Inconelu 713 LC Tvůrce(i) Petrenec, Martin (UFM-A)
Obrtlík, Karel (UFM-A) RID, ORCID
Polák, Jaroslav (UFM-A) RID, ORCIDZdroj.dok. Fracture of Nano and Engineering Materials and Structures : proceedings. - Dordrecht : Springer, 2006 / Gdoutos E.E. - ISBN 1-4020-4971-4
S. 883-884Poč.str. 2 s. Akce European Conference of Fracture /16./ Datum konání 03.07.2006-07.07.2006 Místo konání Alexandroupolis Země GR - Řecko Typ akce WRD Jazyk dok. eng - angličtina Země vyd. NL - Nizozemsko Klíč. slova Dislocation arrangement ; superalloy Inconel 713 LC ; high temperature fatigue Vědní obor RIV JL - Únava materiálu a lomová mechanika CEP 1QS200410502 GA AV ČR - Akademie věd GP106/05/P521 GA ČR - Grantová agentura ČR CEZ AV0Z20410507 - UFM-A (2005-2011) Anotace Dislocation arrangement was studied in cast polycrystalline INCONEL 713LC superalloy cyclically strained to failure at 300K,773K,973K and 1073K temperatures.The characteristic dislocation substructures and their evolution in cyclic straining with different strain amplitudes up to fracture were documented.3D-dimensional dislocation arrangement in individual grains was determined using the technique of oriented foils in transmission electron microscope.Planar dislocation arrangements in the form of bands parallel to the{111}planes were observed in specimens cycled at all temperatures.These bands passing through both the channels and the precipitates are formed as ladder-like bands at room temperature and as thin slabs of high dislocation density at high temperatures.They represent the zones of cyclic plastic strain localization in the material.Surface observation revealed pronounced slip markings with extrusions and intrusions and crack initiation along slip markings at room temperature. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2007
Počet záznamů: 1