Fatigue Crack Initiation Change of Cast AZ91 Magnesium Alloy from Low to Very High Cycle Fatigue Region
SYS 0547378 LBL 01000a^^22220027750^450 005 20230104132133.6 014 $a 85117769933 $2 SCOPUS 014 $a 000718657500001 $2 WOS 017 $a 10.3390/ma14216245 $2 DOI 100 $a 20211101d m y slo 03 ba 101 $a eng $d eng 102 $a CH 200 1-
$a Fatigue Crack Initiation Change of Cast AZ91 Magnesium Alloy from Low to Very High Cycle Fatigue Region 215 $a 11 s. 300 $a https://www.mdpi.com/1996-1944/14/21/6245/htm 463 -1
$1 001 cav_un_epca*0378436 $1 011 $e 1996-1944 $1 200 1 $a Materials $v Roč. 14, č. 21 (2021) $1 205 $a ONLINE $1 210 $c MDPI 610 $a Mg 610 $a fatigue mechanism 610 $a microstructure 610 $a focused ion beam (FIB) 610 $a scanning electron microscopy (SEM) 700 -1
$3 cav_un_auth*0309162 $a Fintová $b Stanislava $p UFM-A $i Vysokocyklová únava $j High cycle fatigue $w High Cycle Fatigue Group $y SK $4 070 $z K $T Ústav fyziky materiálů AV ČR, v. v. i. 701 -1
$3 cav_un_auth*0351864 $a Trško $b L. $y SK $4 070 701 -1
$3 cav_un_auth*0101246 $a Chlup $b Zdeněk $p UFM-A $i Křehký lom $j Brittle fracture $w Brittle Fracture Group $4 070 $T Ústav fyziky materiálů AV ČR, v. v. i. 701 -1
$3 cav_un_auth*0335548 $a Pastorek $b F. $y SK $4 070 701 -1
$3 cav_un_auth*0335550 $a Kajánek $b D. $y SK $4 070 701 -1
$3 cav_un_auth*0101287 $a Kunz $b Ludvík $p UFM-A $i Vysokocyklová únava $j High cycle fatigue $w High Cycle Fatigue Group $4 070 $T Ústav fyziky materiálů AV ČR, v. v. i. 856 $u https://www.mdpi.com/1996-1944/14/21/6245 $9 RIV
Počet záznamů: 1