Fracture behaviour of the 14Cr ODS steel exposed to helium and liquid lead
SYS 0480409 LBL 01000a^^22220027750^450 005 20240103214818.9 014 $a 85018463374 $2 SCOPUS 014 $a 000403132300017 $2 WOS 017 $a 10.1016/j.jnucmat.2017.03.049 $2 DOI 100 $a 20171026d m y slo 03 ba 101 $a eng $d eng 102 $a NL 200 1-
$a Fracture behaviour of the 14Cr ODS steel exposed to helium and liquid lead 215 $a 12 s. 463 -1
$1 001 cav_un_epca*0257060 $1 011 $a 0022-3115 $e 1873-4820 $1 200 1 $a Journal of Nuclear Materials $v Roč. 490, JUL (2017), s. 143-154 $1 210 $c Elsevier 610 $a Impact fracture 610 $a Microanalysis 610 $a Nanostructured steel 610 $a Oxidation 610 $a Thermal ageing 700 -1
$3 cav_un_auth*0286828 $4 070 $a Hojná $b A. $y CZ 701 -1
$3 cav_un_auth*0286829 $4 070 $a Di Gabriele $b F. $y CZ 701 -1
$3 cav_un_auth*0201110 $i Křehký lom $j Brittle fracture $w Brittle Fracture Group $4 070 $a Hadraba $b Hynek $p UFM-A $y CZ $T Ústav fyziky materiálů AV ČR, v. v. i. 701 -1
$3 cav_un_auth*0310096 $i Křehký lom $j Brittle fracture $w Brittle Fracture Group $4 070 $a Husák $b Roman $p UFM-A $y CZ $T Ústav fyziky materiálů AV ČR, v. v. i. 701 -1
$3 cav_un_auth*0243661 $i Nízkocyklová únava $j Low cycle fatigue $w Low Cycle Fatigue Group $4 070 $a Kuběna $b Ivo $p UFM-A $T Ústav fyziky materiálů AV ČR, v. v. i. 701 -1
$3 cav_un_auth*0338864 $4 070 $a Rozumová $b L. $y CZ 701 -1
$3 cav_un_auth*0344922 $4 070 $a Bublíková $b P. $y CZ 701 -1
$3 cav_un_auth*0344921 $4 070 $a Kalivodová $b J. $y CZ 701 -1
$3 cav_un_auth*0101398 $a Matějíček $b Jiří $i Materiálové inženýrství $j Materials Engineering $k MI $l MI $p UFP-V $w Materials Engineering $y CZ $T Ústav fyziky plazmatu AV ČR, v. v. i.