Počet záznamů: 1
Effect of heat treatment on the microstructure and fatigue behaviour of AISI 4130 steel
- 1.
SYSNO ASEP 0578079 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Effect of heat treatment on the microstructure and fatigue behaviour of AISI 4130 steel Tvůrce(i) Poloprudský, Jakub (UFM-A) ORCID
Chlupová, Alice (UFM-A) RID, ORCID
Šulák, Ivo (UFM-A) ORCID
Obrtlík, Karel (UFM-A) RID, ORCIDCelkový počet autorů 4 Zdroj.dok. Kovové materiály. - : Ústav fyziky materiálu AV ČR, v. v. i. - : Ústav materiálov a mechaniky strojov SAV. - : Ústav materiálového výskumu SAV. - : Strojnícka fakulta STU - ISSN 0023-432X
Roč. 61, č. 6 (2023), s. 401-407Poč.str. 7 s. Jazyk dok. eng - angličtina Země vyd. SK - Slovensko Klíč. slova medium carbon steel ; heat treatment ; fatigue life ; microstructure ; scanning electron microscopy Vědní obor RIV JG - Hutnictví, kovové materiály Obor OECD Materials engineering CEP CK02000025 GA TA ČR - Technologická agentura ČR Způsob publikování Open access Institucionální podpora UFM-A - RVO:68081723 UT WOS 001093432600003 EID SCOPUS 85176815681 DOI https://doi.org/10.31577/km.2023.6.401 Anotace AISI 4130 steel is widely used in the aircraft industry, mainly for frame structures. It is
a medium carbon low-alloyed (25CrMo4) steel predetermined for precipitation of carbides in
the microstructure during heat treatment. Six different heat treatments were applied to study
the effect of the resulting microstructure (ferritic-pearlitic in a normalised state or martensitic
with carbides in a hardened state) on the fatigue life of AISI 4130. Tension-tension cycling
under force control was used to determine the S-N curve of flat specimens with a central
circular notch. The best fatigue properties were achieved for the material state HT125, i.e.,
hardened & tempered to 125 ksi (863 MPa), exhibiting the maximum stress at a fatigue limit
of 225 MPa, which is approximately 5–15 % better compared to the rest of the applied heat
treatments. Microstructural investigations using scanning electron microscopy explained the
acquired fatigue life results of AISI 4130 concerning different heat-treated conditions.Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2024 Elektronická adresa http://www.kovmat.sav.sk/article.php?rr=61&cc=6&ss=401
Počet záznamů: 1