Inverse-Heusler Mn2FeSi alloy prepared by powder metallurgy route
- 1.
SYSNO ASEP 0564112 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název Inverse-Heusler Mn2FeSi alloy prepared by powder metallurgy route Tvůrce(i) Životský, O. (CZ)
Skotnicová, K. (CZ)
Čegan, T. (CZ)
Juřica, J. (CZ)
Gembalová, L. (CZ)
Zažímal, František (UFM-A)
Jirásková, Yvonna (UFM-A) RID, ORCID
Szurman, I. (CZ)Celkový počet autorů 8 Zdroj.dok. METAL 2022. - Ostrava : TANGER Ltd., 2022 - ISSN 2694-9296 - ISBN 978-80-88365-06-8 Rozsah stran s. 645-650 Poč.str. 6 s. Forma vydání Online - E Akce METAL 2022 - International Conference on Metallurgy and Materials /31./ Datum konání 18.05.2022 - 19.05.2022 Místo konání Brno Země CZ - Česká republika Typ akce WRD Jazyk dok. eng - angličtina Země vyd. CZ - Česká republika Klíč. slova Heusler alloy, powder, ball milling, microstructure, magnetism ; powder ; ball milling ; microstructure ; magnetism Vědní obor RIV JG - Hutnictví, kovové materiály Obor OECD Materials engineering Institucionální podpora UFM-A - RVO:68081723 EID SCOPUS 85144140311 DOI 10.37904/metal.2022.4434 Anotace The Mn2FeSi inverse-Heusler alloy was prepared by solid-state reactions using ball milling for 168 h in n hexane. Two milling procedures varying in the ball-to-powder ratio, namely 4:1 and 10:1, were used to follow
their influence on alloy formation and its physical properties. In both cases no Heusler structure was obtained
directly and therefore the subsequent annealing at 1223 K for 1.5 h in pure Ar was applied. The energy dispersive X-ray analysis resulted in the chemical composition about 49.0-49.9 at% Mn, 25.3-25.6 at% Fe, and
24.8-25.4 at% Si, in a good agreement with nominal one. X-ray diffraction of both powders confirmed inverse Heusler XA structure of lattice parameters 0.5675 nm (4:1) and 0.5677 nm (10:1), only slightly higher as
theoretically obtained 0.560 nm. The presence of minor oxidation phases was also observed in the particle
structure of powders. Magnetic properties were analysed at low and room temperatures. Both alloys exhibit
paramagnetic behaviour at room temperature confirmed by transmission Mössbauer spectroscopy
measurements. Different magnetic behaviour of alloys is observed below 65 K.Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2025 Elektronická adresa https://www.confer.cz/metal/2022/4434-inverse-heusler-mn2fesi-alloy-prepared-by-powder-metallurgy-route