Corrosion fatigue lifetime assessment of high-speed railway axle EA4T steel with artificial scratch
SYS 0544864 LBL 01000a^^22220027750^450 005 20240103230126.2 014 $a 85100990592 $2 SCOPUS 014 $a 000633033100004 $2 WOS 017 70
$a 10.1016/j.engfracmech.2021.107588 $2 DOI 100 $a 20210823d m y slo 03 ba 101 0-
$a eng $d eng 102 $a GB 200 1-
$a Corrosion fatigue lifetime assessment of high-speed railway axle EA4T steel with artificial scratch 215 $a 13 s. 463 -1
$1 001 cav_un_epca*0252820 $1 011 $a 0013-7944 $e 1873-7315 $1 200 1 $a Engineering Fracture Mechanics $v Roč. 245, MAR (2021) $1 210 $c Elsevier 608 $a Article 610 $a High cycle fatigue 610 $a Defect-tolerant design 610 $a Crack initiation and propagation 610 $a Stress corrosion cracking 610 $a High-speed railway axles 700 -1
$3 cav_un_auth*0274580 $a Hu $b Y. $y CN $4 070 701 -1
$3 cav_un_auth*0222092 $a Wu $b S. $y CN $4 070 701 -1
$3 cav_un_auth*0336421 $a Withers $b P.J. $y GB $4 070 701 -1
$3 cav_un_auth*0412733 $a Cao $b H. $y GB $4 070 701 -1
$3 cav_un_auth*0324912 $a Chen $b P. $y CN $4 070 701 -1
$3 cav_un_auth*0300585 $a Zhang $b Y. $y CN $4 070 701 -1
$3 cav_un_auth*0412734 $a Shen $b Z. $y GB $4 070 701 -1
$3 cav_un_auth*0353603 $a Vojtek $b Tomáš $p UFM-A $i Vysokocyklová únava $j High cycle fatigue $y CZ $4 070 $T Ústav fyziky materiálů AV ČR, v. v. i. 701 -1
$3 cav_un_auth*0101268 $a Hutař $b Pavel $p UFM-A $i Vysokocyklová únava $j High cycle fatigue $4 070 $T Ústav fyziky materiálů AV ČR, v. v. i. 856 $u https://www.sciencedirect.com/science/article/pii/S001379442100059X?via%3Dihub $9 RIV
Počet záznamů: 1