Neutron Diffraction Study of Ti-Zr Alloy Microstructure Evolution during Annealing after Severe Plastic Deformation
- 1.
SYSNO ASEP 0534290 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Neutron Diffraction Study of Ti-Zr Alloy Microstructure Evolution during Annealing after Severe Plastic Deformation Tvůrce(i) Strunz, Pavel (UJF-V) RID, ORCID, SAI
Kunčická, L. (CZ)
Kocich, R. (CZ)
Farkas, Gergely (UJF-V) RID, ORCID, SAI
Macháčková, A. (CZ)
Ryukhtin, Vasil (UJF-V) RID, ORCID, SAICelkový počet autorů 6 Zdroj.dok. Journal of Surface Investigation-X-Ray Synchrotron and Neutron Techniques. - : Pleiades Publishing - ISSN 1027-4510
Roč. 14, SUPPL 1 (2020), s. 225-230Poč.str. 6 s. Forma vydání Tištěná - P Jazyk dok. eng - angličtina Země vyd. US - Spojené státy americké Klíč. slova Ti alloys ; severe plastic deformation ; annealing ; neutron difffraction Vědní obor RIV BM - Fyzika pevných látek a magnetismus Obor OECD Condensed matter physics (including formerly solid state physics, supercond.) CEP GA19-15479S GA ČR - Grantová agentura ČR LM2015056 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy EF16_013/0001794 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Způsob publikování Omezený přístup Institucionální podpora UJF-V - RVO:61389005 UT WOS 000578828100047 EID SCOPUS 85092269642 DOI 10.1134/S1027451020070459 Anotace The evolution of the Ti-Zr alloy microstructure (residual stresses, as well as microstress) during annealing after severe plastic deformation is reported. A strong residual macro-stresses relief starts at temperature of 530-540 degrees C. A steep decrease continues up to 580 degrees C and a further slight decrease up to 600 degrees C. Microstrain (caused by the high dislocation density created by equal channel angular pressing) is almost constant up to 300 degrees C, and then begins to decrease gradually due to recovery. The microstrain decrease accelerates at 560 degrees C and is finished at 580 degrees C. Most probably, this is caused by recrystallization. The information obtained is important for possible microstructure modifications and tuning via post-process heat treatment. Pracoviště Ústav jaderné fyziky Kontakt Markéta Sommerová, sommerova@ujf.cas.cz, Tel.: 266 173 228 Rok sběru 2021 Elektronická adresa https://doi.org/10.1134/S1027451020070459
Počet záznamů: 1