Characterisation of mechanical and fracture behaviour of Al2O3/ZrO2/BaTiO3 laminate by indentation
- 1.
SYSNO ASEP 0531742 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Characterisation of mechanical and fracture behaviour of Al2O3/ZrO2/BaTiO3 laminate by indentation Tvůrce(i) Hadraba, Hynek (UFM-A) RID, ORCID
Chlup, Zdeněk (UFM-A) RID, ORCID
Drdlík, D. (CZ)
Šiška, Filip (UFM-A) RID, ORCIDCelkový počet autorů 4 Zdroj.dok. Journal of the European Ceramic Society. - : Elsevier - ISSN 0955-2219
Roč. 40, č. 14 (2020), s. 4799-4807Poč.str. 9 s. Jazyk dok. eng - angličtina Země vyd. GB - Velká Británie Klíč. slova Laminate ; Electrophoretic deposition ; Barium titanate ; Crack propagation ; Energy harvesting Vědní obor RIV JH - Keramika, žáruvzdorné materiály a skla Obor OECD Ceramics CEP LQ1601 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy GA17-08153S GA ČR - Grantová agentura ČR Způsob publikování Omezený přístup Institucionální podpora UFM-A - RVO:68081723 UT WOS 000556262000012 EID SCOPUS 85083568335 DOI 10.1016/j.jeurceramsoc.2020.04.024 Anotace The paper describes the preparation of laminate piezo-ceramic composite consisting of Al2O3, ZrO2 and BaTiO3 layers and proves the idea of residual stresses utilization for crack deflection and handling with the brittleness of BaTiO3. The laminate was prepared by alternate electrophoretic deposition. Although the laminate was sintered at 1300 degrees C and consisted of layers having a density between 57 % (ZrO2) and 73 % (BaTiO3), the hardness and elastic modulus of layers corresponded to those of free sintered monolithic ceramics at a comparable level of porosity. The crack deflection at the interface between individual layers was observed having the same effect and magnitude as deflection observed in the case of fully dense Al2O3/ZrO2 laminates. An interlayer developed on the interface between Al2O3 and BaTiO3 had no negative impact on crack propagation. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2021 Elektronická adresa https://www.sciencedirect.com/science/article/pii/S0955221920302934?via%3Dihub
Počet záznamů: 1