High-temperature creep of a CoNiCrAlY bond coat alloy
- 1.
SYSNO ASEP 0507171 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název High-temperature creep of a CoNiCrAlY bond coat alloy Tvůrce(i) Dobeš, Ferdinand (UFM-A) RID, ORCID
Dymáček, Petr (UFM-A) RID, ORCID
Hasegawa, M. (JP)
Iwashita, M. (JP)Celkový počet autorů 4 Zdroj.dok. Materials Science and Engineering A Structural Materials Properties Microstructure and Processing. - : Elsevier - ISSN 0921-5093
Roč. 759, JUN (2019), s. 272-277Poč.str. 6 s. Jazyk dok. eng - angličtina Země vyd. CH - Švýcarsko Klíč. slova CoNiCrAlY bond coat alloy ; High entropy alloy ; Creep ; Powder metallurgy ; Zener-Hollomon parameter Vědní obor RIV JG - Hutnictví, kovové materiály Obor OECD Materials engineering CEP EF16_013/0001823 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Způsob publikování Omezený přístup Institucionální podpora UFM-A - RVO:68081723 UT WOS 000472813900030 EID SCOPUS 85065766013 DOI 10.1016/j.msea.2019.05.033 Anotace Creep tests of a CoNiCrAlY bond coat alloy were conducted in the temperature range from 1073 K to 1473 K. The alloy was prepared from a powder with a nominal chemical composition of 34.2% Co, 28.6% Ni, 21.2% Cr, 15.6% Al, 0.4% Y (atomic percent is given throughout) by consolidating it under a stress of 60 MPa and annealing it at 1473 K. The final composition of the alloy is 36.3% Co, 29.6% Ni, 21.0% Cr, 12.8% Al and 0.3% Y. The stress exponent n decreases with the increasing temperature from 3.9 at 1073 K to approximately 1 at 1473 K. Consequently, the activation energy of creep is stress dependent and ranges from 512 kJ/mol to 224 kJ/mol with increasing stress. Combined creep and constant strain rate data can be described by the Garofalo (sinh) equation. A comparison of the results with available creep data of free-standing bond coats is presented. Creep resistance of the present alloy clearly overwhelms the resistance of bond coat alloys previously summarized by Wood. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2020 Elektronická adresa https://www.sciencedirect.com/science/article/pii/S0921509319306446?via%3Dihub
Počet záznamů: 1