Crystal growth, low-temperature spectroscopy and multi-watt laser operation of Yb:Ca.sub.3./sub.NbGa.sub.3./sub.Si.sub.2./sub.O.sub.14./sub.
- 1.
SYSNO ASEP 0492541 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Crystal growth, low-temperature spectroscopy and multi-watt laser operation of Yb:Ca3NbGa3Si2O14 Tvůrce(i) Zhang, X. (ES)
Loiko, P. (RU)
Mateos, X. (ES)
Serres, J.M. (ES)
Ren, J. (CN)
Guo, J. (CN)
Cheng, R. (CN)
Gao, C. (CN)
Dong, Q. (CN)
Jambunathan, Venkatesan (FZU-D)
Lucianetti, Antonio (FZU-D) RID, ORCID
Mocek, Tomáš (FZU-D) RID, ORCID, SAI
Vilejshikova, E. (BY)
Griebner, U. (DE)
Petrov, V. (DE)
Wang, Z. (CN)
Guo, B. (CN)
Xu, X. (CN)
Aguilo, M. (ES)
Diaz, F. (ES)Celkový počet autorů 20 Zdroj.dok. Journal of Luminescence. - : Elsevier - ISSN 0022-2313
Roč. 197, May (2018), s. 90-97Poč.str. 8 s. Jazyk dok. eng - angličtina Země vyd. NL - Nizozemsko Klíč. slova silicate crystals ; ytterbium ; crystal growth ; spectroscopy ; stark splitting ; stimulated emission Vědní obor RIV BH - Optika, masery a lasery Obor OECD Optics (including laser optics and quantum optics) CEP LO1602 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy EF15_006/0000674 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy LM2015086 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Institucionální podpora FZU-D - RVO:68378271 UT WOS 000425996400013 EID SCOPUS 85041489568 DOI 10.1016/j.jlumin.2018.01.004 Anotace We report on the crystal growth, structure, room- and low-temperature (6 K) absorption and emission spectroscopy of a 3 at% Yb3+-doped trigonal ordered langasite-type silicate crystal, Ca3NbGa3Si2O14 (Yb: CNGS). The Rietveld refinement data are presented. Absorption, stimulated-emission and gain cross-sections are determined for the Yb3+ ion in CNGS for p and s polarizations. The maximum stimulated emission cross-section amounts to sigma(SE) = 0.97 x 10(-20) cm(-2) at 10(14) nm (sigma-polarization). The Stark splitting of the Yb3+ multiplets is resolved. Microchip laser operation is obtained with both a-cut and c-cut 3 at% Yb: CNGS samples under endpumping at 976 nm by a Volume Bragg Grating-stabilized diode laser. For the latter cut, the maximum output power reaches 7.61 W at 1048-1060 nm with a slope efficiency of 59%. By varying the output coupling, multiwatt emission over a 50 nm-broad spectral range is achieved. Pracoviště Fyzikální ústav Kontakt Kristina Potocká, potocka@fzu.cz, Tel.: 220 318 579 Rok sběru 2019