Effect of alumina-silica-zirconia eutectic ceramic thermal barrier coating on the low cycle fatigue behaviour of cast polycrystalline nickel-based superalloy at 900 °C
- 1.
SYSNO ASEP 0478233 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Effect of alumina-silica-zirconia eutectic ceramic thermal barrier coating on the low cycle fatigue behaviour of cast polycrystalline nickel-based superalloy at 900 °C Tvůrce(i) Obrtlík, Karel (UFM-A) RID, ORCID
Čelko, L. (CZ)
Chráska, Tomáš (UFP-V) RID, ORCID
Šulák, Ivo (UFM-A) ORCID
Gejdoš, P. (CZ)Celkový počet autorů 5 Zdroj.dok. Surface and Coatings Technology. - : Elsevier - ISSN 0257-8972
Roč. 318, MAY (2017), s. 374-381Poč.str. 8 s. Forma vydání Tištěná - P Akce RIPT - International Meeting on Thermal Spraying /7./ Datum konání 09.12.2015 - 12.12.2015 Místo konání Limoges Země FR - Francie Typ akce WRD Jazyk dok. eng - angličtina Země vyd. CH - Švýcarsko Klíč. slova Thermal barrier coating ; Nickel-based superalloy ; Plasma spraying ; High temperature fatigue ; Fatigue life ; Cyclic stress-strain curve Vědní obor RIV JL - Únava materiálu a lomová mechanika Obor OECD Audio engineering, reliability analysis Vědní obor RIV – spolupráce Ústav fyziky plazmatu - Únava materiálu a lomová mechanika CEP GA15-20991S GA ČR - Grantová agentura ČR Institucionální podpora UFM-A - RVO:68081723 ; UFP-V - RVO:61389021 UT WOS 000402356100045 EID SCOPUS 85014792327 DOI 10.1016/j.surfcoat.2017.03.003 Anotace Cylindrical specimens of nickel-based superalloy Inconel 713LC in an as-cast condition and coated with a thermal barrier coating (TBC) system consisting of a CoNiCrAlY bond coat and a eutectic ceramic alumina-silica-zirconia top coat were cyclically loaded under strain control at 900 °C in air. TBC was deposited using atmospheric plasma spray and water-stabilised plasma spray techniques for the bond coat and the top coat, respectively. The microstructure of the substrate material and the TBC was characterised and the hardness of TBC was measured. The cyclic stress-strain response and fatigue life of both materials were assessed. The stress response of the TBC-coated superalloy is lower than the uncoated superalloy. The detrimental effect of TBC on the Basquin curve is documented. The specimen section and fracture surface observations revealed fatigue damage mechanisms in both the TBC-coated and uncoated specimens, and that finding helps explain the differences in the fatigue behaviour of both materials. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2018
Počet záznamů: 1