Fatigue crack growth in 316L under uniaxial and torsional loading
- 1.
SYSNO ASEP 0468810 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název Fatigue crack growth in 316L under uniaxial and torsional loading Tvůrce(i) Karol, Michal (UFM-A)
Chlupová, Alice (UFM-A) RID, ORCID
Mazánová, Veronika (UFM-A)
Kruml, Tomáš (UFM-A) RID, ORCIDCelkový počet autorů 4 Zdroj.dok. METAL 2016: 25th International Conference on Metallurgy and Materials. - Ostrava : Tanger Ltd., 2016 - ISBN 978-80-87294-67-3 Rozsah stran s. 568-573 Poč.str. 6 s. Forma vydání Nosič - C Akce METAL 2016 - Anniversary International Conference on Metallurgy and Materials /25./ Datum konání 25.05.2016 - 27.05.2016 Místo konání Brno Země CZ - Česká republika Typ akce WRD Jazyk dok. eng - angličtina Země vyd. CZ - Česká republika Klíč. slova 316L austenitic steel ; surface relief ; fatigue Vědní obor RIV JL - Únava materiálu a lomová mechanika CEP GA15-08826S GA ČR - Grantová agentura ČR LM2015069 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Institucionální podpora UFM-A - RVO:68081723 UT WOS 000391251200090 EID SCOPUS 85010749574 Anotace A study of fatigue crack initiation and growth in 316L austenitic stainless steel is reported. Fatigue experiments were performed at room temperature on full cylindrical specimens cycled axially (tension-compression) and on hollow cylindrical specimens tested in reversed torsion. Microstructure and damage evolution (crack initiation and growth) on the surface of mechanically and electrolytically polished specimens were observed using light and electron microscopy. An analysis of the orientation of microcracks and macrocracks which led to failure was made. Axially loaded specimens exhibited presence of several microcracks which resulted in macrocrack propagating perpendicularly to specimen axis. In the case of torsional loading, orientation of macrocrack propagation was dependent on applied load and presence of notches. High amount of short cracks initiated parallel to specimen axis. Long cracks exhibited a tendency to bifurcate with crack branches oriented at approximately 45° to the specimen axis. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2017
Počet záznamů: 1