Cyclic plasticity and strain localization in cast Gamma-TiAl based alloy
- 1.
SYSNO ASEP 0397311 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název Cyclic plasticity and strain localization in cast Gamma-TiAl based alloy Tvůrce(i) Petrenec, Martin (UFM-A)
Polák, Jaroslav (UFM-A) RID, ORCID
Buček, Petr (UFM-A)Celkový počet autorů 3 Zdroj.dok. 11th International conference on the Mechanical Behavior of Materials (ICM). - Amsterdam : Elsevier, 2011 - ISSN 1877-7058 Rozsah stran s. 1390-1395 Poč.str. 6 s. Forma vydání Tištěná - P Akce ICM11 -International Conference on The Mechanical Behavior of Materials /11./ Datum konání 05.06.2011-09.06.2011 Místo konání Lake Como Země IT - Itálie Typ akce WRD Jazyk dok. eng - angličtina Země vyd. NL - Nizozemsko Klíč. slova low cycle fatigue ; lamellar TiAl alloy ; loop shape parameter ; peristent slip marketing Vědní obor RIV JJ - Ostatní materiály CEP GAP107/11/0704 GA ČR - Grantová agentura ČR UT WOS 000300451301068 EID SCOPUS 80052959968 DOI 10.1016/j.proeng.2011.04.231 Anotace Cyclic strain localization and observation of surface relief in nearly lamellar cast Gamma-TiAl based alloy Ti–48Al–2Nb–2Cr–0.82B (all in at. %) cycled in strain control were experimentally studied. Hysteresis loop area, the cyclic hardening curves, the cyclic stress-strain curve and VH parameter were measured. Surface relief of cyclically strained specimens was observed using scanning electron microscopy. The variations of the VH parameter indicate the cyclic slip localization. The localization has a pronounced effect on surface relief formation. Persistent slip markings are formed on the surface along interlamellar interfaces gamma/aplha2 and gamma/gamma. These locations were nuclei for fatigue cracks in the interior of grains. Experimental results concerning the loop shape parameter and surface relief are used to discuss the role of cyclic slip localization on the cyclic stress-strain response and fatigue crack initiation. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2014
Počet záznamů: 1