Porous Alumina and Zirconia Ceramics With Tailored Thermal Conductivity
- 1.
SYSNO ASEP 0392788 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Porous Alumina and Zirconia Ceramics With Tailored Thermal Conductivity Tvůrce(i) Gregorová, E. (CZ)
Pabst, W. (CZ)
Sofer, Z. (CZ)
Jankovský, O. (CZ)
Matějíček, Jiří (UFP-V) RID, ORCIDCelkový počet autorů 5 Zdroj.dok. Journal of Physics: Conference Series. - : Institute of Physics Publishing - ISSN 1742-6588
Roč. 395, č. 1 (2012), 012022-012022Poč.str. 8 s. Forma vydání Tištěná - P Akce European Thermal Sciences Conference (Eurotherm)/6./ Datum konání 04.09.2012-07.09.2012 Místo konání Poitiers Země FR - Francie Typ akce EUR Jazyk dok. eng - angličtina Země vyd. GB - Velká Británie Klíč. slova Ceramics ; alumina ; zirconia ; porosity ; thermal conductivity ; pore-forming agent ; oxide ceramics ; starch ; porosity Vědní obor RIV JK - Koroze a povrchové úpravy materiálů Institucionální podpora UFP-V - RVO:61389021 UT WOS 000312264800022 DOI 10.1088/1742-6596/395/1/012022 Anotace The thermal conductivity of porous ceramics can be tailored by slip casting and uniaxial dry pressing, using either fugitive pore formers (saccharides) or partial sintering. Porous alumina and zirconia ceramics have been prepared using appropriate powder types (ungranulated for casting, granulated for pressing) and identical firing regimes (but different maximum temperatures in the case of partial sintering). Thermal diffusivities have been measured by the laser- and xenon-flash method and transformed into relative thermal conductivities, which enable a temperature-independent comparison between different materials. While the porosity can be controlled in a similar way for both materials when using pore formers, partial sintering exhibits characteristic differences between alumina and zirconia (for alumina porosities below 45 %, full density above 1600 °C, for zirconia porosities below 60 %, full density above 1300 °C). The different compaction behavior of alumina and zirconia Pracoviště Ústav fyziky plazmatu Kontakt Vladimíra Kebza, kebza@ipp.cas.cz, Tel.: 266 052 975 Rok sběru 2014
Počet záznamů: 1