Lifetime prediction of HDPE pipes grade
- 1.
SYSNO ASEP 0354108 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název Lifetime prediction of HDPE pipes grade Tvůrce(i) Nezbedová, E. (CZ)
Hutař, Pavel (UFM-A) RID, ORCID
Ševčík, Martin (UFM-A) RID
Náhlík, Luboš (UFM-A) RID, ORCID
Knésl, Zdeněk (UFM-A)Celkový počet autorů 5 Zdroj.dok. European Conference on Fracture, 18. - Berlin : Deutscher Verband fur Materialforschung und prufung e.V, 2010 / Klingbeil D. ; Vormwald M. ; Eulitz G. - ISBN 978-3-00-031802-3 Rozsah stran s. 1-9 Poč.str. 9 s. Forma vydání CD-ROM - CD-ROM Akce 18th European Conference on Fracture Datum konání 30.08.2010-03.09.2010 Místo konání Dresden Země DE - Německo Typ akce WRD Jazyk dok. eng - angličtina Země vyd. DE - Německo Klíč. slova HDPE ; creep crack ; time to rupture curve ; PENT test ; pipe failure Vědní obor RIV JL - Únava materiálu a lomová mechanika CEP GA106/08/1409 GA ČR - Grantová agentura ČR GC101/09/J027 GA ČR - Grantová agentura ČR GA106/09/0279 GA ČR - Grantová agentura ČR CEZ AV0Z20410507 - UFM-A (2005-2011) Anotace This paper presents the results of notch tests on single edge notch specimen under condition corresponding to the PENT approach, i.e. at temperature 80°C and nominal stress 2,4 MPa. Tests were performed for one monomodal and two bimodal HDPE materials, both from structural and fracture mechanics point of view. The dependence of a crack opening displacement COD vs. time was measured and the values of the rate of the stable crack growth rate da/dt and time to fracture tf were estimated. To estimate the residual life of pipes the finite element model with an initial defect was suggested and the values of the stress intensity factor K have been calculated. The computation took into account the change of the crack shape during its growth in the pipe. For assessment of the residual service life of pipes the relation da/dt = A (K)m was applied. The values of the pipe life-time for three studied materials are compared and diagram of the hoop stress versus failure time is presented. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2011
Počet záznamů: 1