Polarization-Resolved Position-Sensitive Self-Powered Binary Photodetection in Multilayer Janus CrSBr
- 1.
SYSNO ASEP 0581747 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Polarization-Resolved Position-Sensitive Self-Powered Binary Photodetection in Multilayer Janus CrSBr Tvůrce(i) Panda, Jaganandha (UFCH-W)
Sahu, Satyam (UFCH-W)
Haider, Golam (UFCH-W) ORCID, RID
Thakur, Mukesh Kumar (UFCH-W)
Mosina, K. (CZ)
Velický, Matěj (UFCH-W) ORCID, RID, SAI
Vejpravová, J. (CZ)
Sofer, Z. (CZ)
Kalbáč, Martin (UFCH-W) RID, ORCIDZdroj.dok. ACS Applied Materials and Interfaces. - : American Chemical Society - ISSN 1944-8244
Roč. 16, č. 1 (2024), s. 1033-1043Poč.str. 11 s. Jazyk dok. eng - angličtina Země vyd. US - Spojené státy americké Klíč. slova black phosphorus ; high-performance ; schottky ; photoluminescence ; anisotropy ; graphene ; symmetry ; optical polarization detection ; Janus 2Dlayer ; CrSBr ; self-powered photodetector ; position sensitivity Vědní obor RIV CF - Fyzikální chemie a teoretická chemie Obor OECD Physical chemistry CEP GX20-08633X GA ČR - Grantová agentura ČR Způsob publikování Open access Institucionální podpora UFCH-W - RVO:61388955 UT WOS 001140897400001 EID SCOPUS 85181826871 DOI 10.1021/acsami.3c13552 Anotace Recent progress in polarization-resolved photodetection based on low-symmetry 2D materials has formed the basis of cutting-edge optoelectronic devices, including quantum optical communication, 3D image processing, and sensing applications. Here, we report an optical polarization-resolving photodetector (PD) fabricated from multilayer semiconducting CrSBr single crystals with high structural anisotropy. We have demonstrated self-powered photodetection due to the formation of Schottky junctions at the Au-CrSBr interfaces, which also caused the photocurrent to display a position-sensitive and binary nature. The self-biased CrSBr PD showed a photoresponsivity of similar to 0.26 mA/W with a detectivity of 3.4 x 10(8 )Jones at 514 nm excitation of fluency (0.42 mW/cm(2)) under ambient conditions. The optical polarization-induced photoresponse exhibits a large dichroic ratio of 3.4, while the polarization is set along the a- and the b-axes of single-crystalline CrSBr. The PD also showed excellent stability, retaining >95% of the initial photoresponsivity in ambient conditions for more than five months without encapsulation. Thus, we demonstrate CrSBr as a fascinating material for ultralow-powered optical polarization-resolving optoelectronic devices for cutting-edge technology. Pracoviště Ústav fyzikální chemie J.Heyrovského Kontakt Michaela Knapová, michaela.knapova@jh-inst.cas.cz, Tel.: 266 053 196 Rok sběru 2025 Elektronická adresa https://hdl.handle.net/11104/0349904