Black aluminum-coated Pt/Pb(Zr.sub.0.56./sub.Ti.sub.0.44./sub.)0.sub.3./sub./Pt thin film structures for pyroelectric energy harvesting from a light source
- 1.
SYSNO ASEP 0518875 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Black aluminum-coated Pt/Pb(Zr0.56Ti0.44)03/Pt thin film structures for pyroelectric energy harvesting from a light source Tvůrce(i) More Chevalier, Joris (FZU-D) ORCID
Yudin, Petr (FZU-D) ORCID
Cibert, C. (FR)
Bednyakov, Petr (FZU-D) RID, ORCID
Fitl, P. (CZ)
Valenta, J. (CZ)
Novotný, Michal (FZU-D) RID, ORCID, SAI
Savinov, Maxim (FZU-D) RID, ORCID
Poupon, Morgane (FZU-D) ORCID
Zikmund, Tomáš (FZU-D)
Poullain, G. (FR)
Lančok, Ján (FZU-D) RID, ORCIDCelkový počet autorů 12 Číslo článku 214501 Zdroj.dok. Journal of Applied Physics. - : AIP Publishing - ISSN 0021-8979
Roč. 126, č. 21 (2019), s. 1-7Poč.str. 7 s. Jazyk dok. eng - angličtina Země vyd. US - Spojené státy americké Klíč. slova PZT films ; energy harvestor ; ferroelectric materials ; thin films ; optical propertie ; pyroelectricity Vědní obor RIV BM - Fyzika pevných látek a magnetismus Obor OECD Condensed matter physics (including formerly solid state physics, supercond.) CEP EF16_019/0000760 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy EF16_013/0001406 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy LO1409 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy GA18-09347S GA ČR - Grantová agentura ČR LM2015088 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Způsob publikování Omezený přístup Institucionální podpora FZU-D - RVO:68378271 UT WOS 000504007300018 EID SCOPUS 85075929056 DOI 10.1063/1.5130538 Anotace A black aluminum (B-Al) film was deposited onto the surface of a stack structure of platinum/Pb(ZrxTi1 − x)O3/platinum (Pt/PZT/Pt) to convert light into a heat variation and the heat variation into a polarization change. A comparison was performed between B-Al/Pt/PZT/Pt and conventional Pt/PZT/Pt structures. An absorbance higher than 95% was measured for the B-Al layer over a large range of wavelengths varying from 350 nm to 1000 nm. The theoretical model shows that heat diffusion was extremely fast through the layers, and the sample holder played a key role in the variation and stabilization of the system temperature. A doubled variation of the polarization was observed when the light was applied onto the surface of the stack structure with stable B-Al on the top. This behavior was interpreted by the larger temperature variations induced under the highly absorptive B-Al layers, in good correlation with the theoretical model prediction based on the heat fluxes in the structures. Pracoviště Fyzikální ústav Kontakt Kristina Potocká, potocka@fzu.cz, Tel.: 220 318 579 Rok sběru 2020 Elektronická adresa https://doi.org/10.1063/1.5130538