Recoverability of large strains and deformation twinning in martensite during tensile deformation of NiTi shape memory alloy polycrystals
- 1.
SYSNO ASEP 0511540 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Recoverability of large strains and deformation twinning in martensite during tensile deformation of NiTi shape memory alloy polycrystals Tvůrce(i) Chen, Y.C. (CN)
Molnárová, Orsolya (FZU-D) ORCID
Tyc, Ondřej (FZU-D) ORCID
Kadeřávek, Lukáš (FZU-D) ORCID
Heller, Luděk (FZU-D) RID, ORCID
Šittner, Petr (FZU-D) RID, ORCIDCelkový počet autorů 6 Zdroj.dok. Acta Materialia. - : Elsevier - ISSN 1359-6454
Roč. 180, Nov (2019), s. 243-259Poč.str. 17 s. Jazyk dok. eng - angličtina Země vyd. GB - Velká Británie Klíč. slova plastic-deformation ; localized deformation ; b2 phase ; transformation ; temperature ; mechanisms ; behavior ; wires ; energetics ; slip ; NiTi ; superelasticity ; shape memory alloy ; tensile test ; large deformation ; martensitic transformation ; deformation twinning ; transmission electron microscopy Vědní obor RIV BM - Fyzika pevných látek a magnetismus Obor OECD Condensed matter physics (including formerly solid state physics, supercond.) CEP EF16_019/0000760 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy LM2015088 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy GC17-00393J GA ČR - Grantová agentura ČR GA18-03834S GA ČR - Grantová agentura ČR Způsob publikování Omezený přístup Institucionální podpora FZU-D - RVO:68378271 UT WOS 000495519100024 EID SCOPUS 85072273148 DOI 10.1016/j.actamat.2019.09.012 Anotace Superelastic NiTi wires were deformed in tension up to gradually increasing total strains at various temperatures, recoverable strains were evaluated and lattice defects left in the microstructure of deformed wires were analyzed by TEM. The recoverable strains evaluated in tensile tests: i) are surprisingly large - exceed 10% strain at low temperatures T ≤ 20 °C, ii) are not significantly restricted by large plastic deformation up to 55% at low temperatures, iii) display local maxima in dependence on total strain in tensile tests at low temperatures, iv) decrease with increasing test temperatures and iv) increase with increasing total strain in tensile tests at high temperatures T ≥ 50 °C. Besides slip dislocations, key lattice defects created by the tensile deformation beyond the martensite yield point are deformation bands containing {114} austenite twins or R-phase. No other austenite twins were found statistically relevant.
Pracoviště Fyzikální ústav Kontakt Kristina Potocká, potocka@fzu.cz, Tel.: 220 318 579 Rok sběru 2020 Elektronická adresa https://doi.org/10.1016/j.actamat.2019.09.012