HYDROGENATION PROPERTIES OF Mg-Al-Ti-Zr-C COMPOSITE
- 1.
SYSNO ASEP 0473833 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název HYDROGENATION PROPERTIES OF Mg-Al-Ti-Zr-C COMPOSITE Tvůrce(i) Král, Lubomír (UFM-A) RID, ORCID
Čermák, Jiří (UFM-A) RID, ORCID
Roupcová, Pavla (UFM-A) RID, ORCIDCelkový počet autorů 3 Zdroj.dok. NANOCON 2016. 8th International Conference on Nanomaterials - Research and Application. Conference Proceedings. - Ostrava : Tanger, 2017 - ISBN 978-80-87294-71-0 Rozsah stran s. 75-79 Poč.str. 5 s. Forma vydání Nosič - C Akce NANOCON 2016. International Conference on Nanomaterials - Research and Application /8./ Datum konání 19.10.2016 - 21.10.2016 Místo konání Brno Země CZ - Česká republika Typ akce WRD Jazyk dok. eng - angličtina Země vyd. CZ - Česká republika Klíč. slova Hydrides ; hydrogen storage ; catalysis ; hydrogen ; Mg-alloys Vědní obor RIV BJ - Termodynamika Obor OECD Thermodynamics CEP LQ1601 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Institucionální podpora UFM-A - RVO:68081723 UT WOS 000410656100012 EID SCOPUS 85017279739 Anotace The improvement of hydrogen storage properties of ball-milled Mg-Al-Ti-Zr-C composite was studied in this
paper. It has been previously shown, that the addition of Ti, Zr, Al and C improves storage properties of Mg.
This beneficial effect of additives upon hydrogen storage properties can be explained by catalysis by the
nanoparticles rich in Ti, Zr or Al located on the surface of Mg grains. They provide effective pathways for the
hydrogen diffusion into the MgH2. The morphological and microstructural characteristics were investigated by
scanning electron microscope Tescan Lyra 3 and by X-ray diffraction. The hydrogen sorption was measured
by Sieverts method using Setaram PCT-Pro device.
Studied experimental composite absorbed 4.2 wt.% H 2 at 573 K and 3 wt.% H 2 at 523K within 10 min. The
hydrogen storage capacity of the composite was about 4.6% wt.% H 2 and 4.2% wt.% H 2 at 573K and 523K,
respectively.Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2018