Microstructural changes during deformation of AISI 300 grade austenitic stainless steels: Impact of chemical heterogeneity
- 1.
SYSNO ASEP 0465434 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název Microstructural changes during deformation of AISI 300 grade austenitic stainless steels: Impact of chemical heterogeneity Tvůrce(i) Man, Jiří (UFM-A) RID, ORCID
Kuběna, Ivo (UFM-A) RID, ORCID
Smaga, M. (DE)
Man, O. (CZ)
Järvenpää, A. (FI)
Weidner, A. (DE)
Chlup, Zdeněk (UFM-A) RID, ORCID
Polák, Jaroslav (UFM-A) RID, ORCIDCelkový počet autorů 8 Zdroj.dok. 21st European Conference on Fracture. - Amsterdam : Elsevier, 2016 - ISSN 2452-3216 Rozsah stran s. 2299-2306 Poč.str. 8 s. Forma vydání Online - E Akce ECF21 - European Conference on Fracture /21./ Datum konání 20.06.2016-24.06.2016 Místo konání Catania Země IT - Itálie Typ akce WRD Jazyk dok. eng - angličtina Země vyd. NL - Nizozemsko Klíč. slova austenitic stainless steels ; deformation induced martensite ; chemical banding ; UFG structure ; color metallography Vědní obor RIV JL - Únava materiálu a lomová mechanika CEP GA13-32665S GA ČR - Grantová agentura ČR Institucionální podpora UFM-A - RVO:68081723 UT WOS 000387976802045 DOI 10.1016/j.prostr.2016.06.288 Anotace The importance of chemical heterogeneity for destabilization of austenitic structure and formation of deformation induced martensite (DIM) in AISI 300 grade austenitic stainless steels (ASSs) of different level of austenite stability (316L, 304, 301LN) is pointed out. Color etching reveals that the structure of wrought Cr–Ni type steels of diverse wrought semi-product forms (plates, sheets, bars) is never fully chemically homogeneous. Confrontation of distribution and morphology of DIM after static and cyclic straining with the characteristic local variations in chemical composition proved prominent role of chemical banding in the destabilization of originally fully austenitic structure. This fact should be considered especially when interpreting the results of hydrogen embrittlement tensile testing of Cr–Ni ASSs with lowered Ni content. An impact of chemical heterogeneity on microstructural changes during production of UFG structure of 301LN and its cyclic straining is highlighted. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2017
Počet záznamů: 1