Influence of Al-Cr diffusion coating on low cycle fatigue behavior of cast nickel-base superalloy at 800 °C
- 1.
SYSNO ASEP 0387434 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název Influence of Al-Cr diffusion coating on low cycle fatigue behavior of cast nickel-base superalloy at 800 °C Tvůrce(i) Obrtlík, Karel (UFM-A) RID, ORCID
Pospíšilová, S. (CZ)
Juliš, M. (CZ)
Podrábský, T. (CZ)
Kruml, Tomáš (UFM-A) RID, ORCIDCelkový počet autorů 5 Zdroj.dok. 19th European Conference on Fracture: Fracture Mechanics for Durability, Reliability and Safety. - Kazan : Kazan Scientific Centre of the RAS, 2012 / Klingbeil D. ; Vormwald M. ; Eulitz G. - ISBN 978-5-905576-18-8 Rozsah stran paper no. 330 Poč.str. 7 s. Forma vydání Nosič - C Akce 19th European Conference on Fracture:Fracture Mechanics for Durability, Reliability and Safety Datum konání 26.08.2012-31.08.2012 Místo konání Kazan Země RU - Rusko Typ akce WRD Jazyk dok. eng - angličtina Země vyd. RU - Rusko Klíč. slova Inconel 713LC ; diffusion coating ; Low cycle fatigue Vědní obor RIV JL - Únava materiálu a lomová mechanika CEP GAP107/11/2065 GA ČR - Grantová agentura ČR Institucionální podpora UFM-A - RVO:68081723 Anotace High temperature low cycle fatigue behavior of the cast nickel-based superalloy Inconel 713LC in as-received condition and coated with an Al-Cr diffusion layer have been investigated. The diffusion coating was deposited using the CVD out of pack technique. It was characterized and the hardness depth profile was measured. Fatigue tests were performed at 800 °C in air using cylindrical specimens. Cyclic hardening/softening curves, cyclic stress-strain curve and fatigue life curves were obtained. The detrimental effect of the surface treatment on the Manson-Coffin and the derived Wöhler curves is documented. Fracture surface and surface relief observations and examinations of specimen sections help to discuss the effect of the diffusion coating on the fatigue life. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2013
Počet záznamů: 1