Effect of cyclic loading on the microstructure of thin zirconia tapes
- 1.
SYSNO ASEP 0572425 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Effect of cyclic loading on the microstructure of thin zirconia tapes Tvůrce(i) Šťastný, P. (CZ)
Chlup, Zdeněk (UFM-A) RID, ORCID
Hlinican, J. (CZ)
Kaštyl, J. (CZ)
Trunec, M. (CZ)Celkový počet autorů 5 Zdroj.dok. Journal of the European Ceramic Society. - : Elsevier - ISSN 0955-2219
Roč. 43, č. 10 (2023), s. 4498-4505Poč.str. 8 s. Jazyk dok. eng - angličtina Země vyd. GB - Velká Británie Klíč. slova Yttrium oxide ; Fatigue ; Tape casting ; Microstructure ; Transformation Vědní obor RIV JH - Keramika, žáruvzdorné materiály a skla Obor OECD Ceramics Výzkumná infrastruktura CzechNanoLab - 90110 - Vysoké učení technické v Brně Způsob publikování Omezený přístup Institucionální podpora UFM-A - RVO:68081723 UT WOS 000983895300001 EID SCOPUS 85150805682 DOI 10.1016/j.jeurceramsoc.2023.03.024 Anotace The effect of cyclic loading on the microstructure and the phase composition of thin zirconia tapes was studied. Zirconium oxide stabilized with 3 mol% of yttrium was used for preparing the tapes by the gel-tape casting method. The static and cyclic strengths of the samples with a thickness of approximately 0.2 mm were tested. The average static strength of 1233 MPa was determined in a three-point bend configuration. The maximal flexural stress during cyclic loading had to be kept below 900 MPa to ensure the failure-free performance of the tapes(107 cycles). No evidence of an excessive transformation of the tetragonal microstructure induced by cyclic loading was found. The transformation toughening mechanism of the tetragonal microstructure was not significantly affected by cyclic loading. Based on the results, thin flexible 3Y-TZP parts possess a low risk of mechanically induced excessive transformational microstructural changes during the service life of the part. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2024 Elektronická adresa https://www.sciencedirect.com/science/article/pii/S0955221923002157?via%3Dihub
Počet záznamů: 1