An ultrasonic study of relaxation processes in pure and mechanically alloyed tungsten
- 1.
SYSNO ASEP 0537989 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název An ultrasonic study of relaxation processes in pure and mechanically alloyed tungsten Tvůrce(i) Koller, Martin (UT-L) ORCID
Vilémová, Monika (UFP-V) RID, ORCID
Lukáč, František (UFP-V) ORCID
Beran, Přemysl (UJF-V) RID, ORCID, SAI
Čížek, B. (CZ)
Hadraba, Hynek (UFM-A) RID, ORCID
Matějíček, Jiří (UFP-V) RID, ORCID
Veverka, Jakub (UFP-V) ORCID
Seiner, H. (CZ)Celkový počet autorů 9 Číslo článku 105233 Zdroj.dok. International Journal of Refractory Metals & Hard Materials. - : Elsevier - ISSN 0263-4368
Roč. 90, August (2020)Poč.str. 7 s. Forma vydání Tištěná - P Jazyk dok. eng - angličtina Země vyd. GB - Velká Británie Klíč. slova fine-grained tungsten ; oxide dispersion ; resonant ultrasound spectroscopy ; ductile-to-brittle transition temperature ; internal friction ; dislocation density Vědní obor RIV BI - Akustika a kmity Obor OECD Acoustics Vědní obor RIV – spolupráce Ústav fyziky plazmatu - Průmyslové procesy a zpracování
Ústav jaderné fyziky - Fyzika pevných látek a magnetismus
Ústav fyziky materiálu - Hutnictví, kovové materiályCEP EF16_019/0000778 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy LM2015056 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Výzkumná infrastruktura Reactors LVR-15 and LR-0 II - 90120 - Centrum výzkumu Řež s.r.o. Způsob publikování Omezený přístup Institucionální podpora UT-L - RVO:61388998 ; UFP-V - RVO:61389021 ; UFM-A - RVO:68081723 ; UJF-V - RVO:61389005 UT WOS 000527310900007 EID SCOPUS 85082173041 DOI 10.1016/j.ijrmhm.2020.105233 Anotace High-temperature internal friction in a pure tungsten single crystal, polycrystals with different grain sizes, and mechanically alloyed tungsten polycrystals was studied. Positron annihilation spectroscopy was used to prove that all studied materials contain a detectable amount of dislocations. Then, resonant ultrasound spectroscopy was applied to determine the internal friction evolution with temperature from room temperature up to 740 degrees C. For the pure tungsten samples, a sharp increase of internal friction was observed for temperatures above 470 degrees C (for the single crystal) or above 400 degrees C (for the polycrystals), the activation energy corresponding to this increase was the same as the activation energy for the ductile-to-brittle transition in tungsten reported in the literature. For the alloyed materials, direct observation of the onset of this relaxation mechanism was impossible due to additional effects resulting from the secondary phases in the material.
Pracoviště Ústav termomechaniky Kontakt Marie Kajprová, kajprova@it.cas.cz, Tel.: 266 053 154 ; Jana Lahovská, jaja@it.cas.cz, Tel.: 266 053 823 Rok sběru 2021 Elektronická adresa https://www.sciencedirect.com/science/article/abs/pii/S0263436820301098