Preparation and characterization of novel environmentally friendly Al2O3/SiO2/CaO ceramic foams
- 1.
SYSNO ASEP 0494817 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Preparation and characterization of novel environmentally friendly Al2O3/SiO2/CaO ceramic foams Tvůrce(i) Bertolla, Luca (UFM-A) ORCID
Chlup, Zdeněk (UFM-A) RID, ORCID
Tatarko, P. (SK)
Hanzel, P. (SK)
Ševeček, O. (CZ)
Roupcová, Pavla (UFM-A) RID, ORCID
Dlouhý, Ivo (UFM-A) RID, ORCIDCelkový počet autorů 7 Zdroj.dok. Ceramics International. - : Elsevier - ISSN 0272-8842
Roč. 44, č. 15 (2018), s. 19063-19069Poč.str. 7 s. Forma vydání Tištěná - P Jazyk dok. eng - angličtina Země vyd. GB - Velká Británie Klíč. slova Porous ceramics ; Silicates ; Thermal diffusivity ; Compressive strength Vědní obor RIV JH - Keramika, žáruvzdorné materiály a skla Obor OECD Ceramics Institucionální podpora UFM-A - RVO:68081723 UT WOS 000445993000192 EID SCOPUS 85050105219 DOI 10.1016/j.ceramint.2018.07.107 Anotace Low-cost Al2O3-SiO2-CaO ceramic foams were prepared using a novel and simple reactive foaming process. The foamed green bodies were produced by mixing aluminium powder and calcium hydroxide in an aqueous solution of sodium silicate and sintered in an argon atmosphere using a pressureless electric current assisted process (T = 800 C). An additional thermal treatment was performed in air using a conventional furnace (T = 1050 degrees C) in order to oxidize the residual metallic phases. The resulting foams exhibited open porosity, densities ranging from 0.50 to 0.65 g/cm(3) and wide pore size distribution (0.04-400 mu m). The compressive strength and thermal diffusivity of these foams ranged from 2.12 to 1.01 MPa and from 0.27 to 0.45 mm(2)s(-1), respectively, which indicate their suitability as thermal insulator materials. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2019
Počet záznamů: 1