Zr alloy protection against high-temperature oxidation: coating by a double-layered structure with active and passive functional properties
- 1.
SYSNO ASEP 0540178 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Zr alloy protection against high-temperature oxidation: coating by a double-layered structure with active and passive functional properties Tvůrce(i) Kratochvílová, Irena (FZU-D) RID, ORCID, SAI
Ashcheulov, Petr (FZU-D) ORCID, RID
Škarohlíd, J. (CZ)
Škoda, R. (CZ)
Kopeček, Jaromír (FZU-D) RID, ORCID
Sajdl, P. (CZ)
Macák, J. (CZ)
Lajčinová, M. (CZ)
Nováková, A. (CZ)
Neethling, J. (ZA)
van Vuuren, A. J. (ZA)
Ngongo, S. (ZA)
Xu, P. (US)
Lorinčík, J. (CZ)
Steinbrück, M. (DE)Celkový počet autorů 15 Číslo článku 108270 Zdroj.dok. Corrosion Science. - : Elsevier - ISSN 0010-938X
Roč. 163, Feb (2020), s. 1-11Poč.str. 11 s. Jazyk dok. eng - angličtina Země vyd. GB - Velká Británie Klíč. slova high temperature corrosion ; Zr nuclear tubes ; double layer protective coating ; nanocrystalline diamond coating ; CrAlSiN Vědní obor RIV BM - Fyzika pevných látek a magnetismus Obor OECD Condensed matter physics (including formerly solid state physics, supercond.) CEP EF16_019/0000760 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy TK02030069 GA TA ČR - Technologická agentura ČR EF16_013/0001406 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy LO1409 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy LM2015088 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Způsob publikování Omezený přístup Institucionální podpora FZU-D - RVO:68378271 UT WOS 000513295700038 EID SCOPUS 85076047855 DOI 10.1016/j.corsci.2019.108270 Anotace In this work, a new concept of metal surface protection against degradation caused by high-temperature oxidation in water environment is presented. We were the first to create a double-layered coating consisting of an active and passive part to protect Zr alloy surface against high-temperature oxidation in a hot water environment. We investigated the hot steam corrosion of ZIRLO fuel cladding coated with a double layer consisting of 500 nm nanocrystalline diamond (NCD) as the bottom layer and 2 μm chromium-aluminum-silicon nitride (CrAlSiN) as the upper layer. Coated and uncoated ZIRLO samples were exposed for 4 days at 400 °C in an autoclave and for 60 min at 1000 °C (nuclear reactor accident temperature) in a hot steam furnace. We have shown that the NCD coating protects the Zr alloy surface against oxidation in an active way: carbon from NCD layer enters the Zr alloy surface and, by changing the physical and chemical properties of the Zr cladding tube surface. Pracoviště Fyzikální ústav Kontakt Kristina Potocká, potocka@fzu.cz, Tel.: 220 318 579 Rok sběru 2021 Elektronická adresa https://doi.org/10.1016/j.corsci.2019.108270