SYSNO ASEP 0494366 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název Stable Ce4+ centres - a tool to optimize cathodoluminescence performance in garnet scintillators Tvůrce(i) Lalinský, Ondřej (UPT-D) RID, ORCID, SAI
Schauer, Petr (UPT-D) RID, SAI, ORCID
Rathaiah, M. (CZ)
Kučera, M. (CZ)Celkový počet autorů 4 Zdroj.dok. Recent Trends in Charged Particle Optics and Surface Physics Instrumentation. Proceedings of the 16th International Seminar. - Brno : Institute of Scientific Instruments The Czech Academy of Sciences, 2018 - ISBN 978-80-87441-23-7 Rozsah stran s. 44-45 Poč.str. 2 s. Forma vydání Tištěná - P Akce Recent Trends in Charged Particle Optics and Surface Physics Instrumentation Datum konání 04.06.2018 - 08.06.2018 Místo konání Skalský dvůr Země CZ - Česká republika Typ akce WRD Jazyk dok. eng - angličtina Země vyd. CZ - Česká republika Klíč. slova garnet scintillators ; cathodoluminescence performance Vědní obor RIV JA - Elektronika a optoelektronika, elektrotechnika Obor OECD Electrical and electronic engineering CEP TE01020118 GA TA ČR - Technologická agentura ČR GA16-05631S GA ČR - Grantová agentura ČR LO1212 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy ED0017/01/01 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Institucionální podpora UPT-D - RVO:68081731 UT WOS 000450591400016 Anotace Garnet single crystals are widely used as scintillators in electron detectors. Cerium activated lutetium aluminum garnet Cex:Lu3-xAl5O12 (LuAG:Ce) is a promising example of such material for these applications. This is mainly due to its high light yield (LY) of 25 kph/MeV, short decay time of 60–80 ns, high atomic density (6.7 g/cm3), and high radiation stability with no hygroscopicity. The cathodoluminescence (CL) performance can be improved by Ga and Gd doping the garnet matrix. Proper admixture of these elements can increase the LY to 50–60 kph/MeV in addition to eliminating unwanted slower decay components. There was an idea that further decay acceleration can be achieved by doping the garnet with monovalent (Li+) or divalent ions (Mg2+, Ca2+). This should increase the valency of some Ce3+ centres to Ce4+ which should better compete with electron traps, and thus accelerate the decay. Our previous work proved the same decay trend, however, at a price of the LY. Such LY loss may induce the idea, if the stable Ce4+ centres are really participating in Ce3+ emission. Pracoviště Ústav přístrojové techniky Kontakt Martina Šillerová, sillerova@ISIBrno.Cz, Tel.: 541 514 178 Rok sběru 2019
Počet záznamů: 1