Development of Creep Damage in Similar Weld Joints of P92 Steel Pipe
- 1.
SYSNO ASEP 0484138 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název Development of Creep Damage in Similar Weld Joints of P92 Steel Pipe Tvůrce(i) Král, Petr (UFM-A) RID, ORCID
Sklenička, Václav (UFM-A) RID, ORCID
Kuchařová, Květa (UFM-A) RID, ORCID
Svobodová, M. (CZ)
Kvapilová, Marie (UFM-A) RID, ORCID
Dvořák, Jiří (UFM-A) RID, ORCIDCelkový počet autorů 6 Zdroj.dok. Contribution of Metallography to Production Problem Solutions II. - Zürich : Trans Tech Publications Ltd, 2017 / Kasl J. - ISSN 1662-9779 - ISBN 978-3-0357-1241-4 Rozsah stran s. 162-167 Poč.str. 6 s. Forma vydání Tištěná - P Akce CCMPPS 2017 - Conference on Contribution of Metallography to Production Problem Solutions /14./ Datum konání 06.06.2017 - 08.06.2017 Místo konání Mariánske Lázně Země CZ - Česká republika Typ akce EUR Jazyk dok. eng - angličtina Země vyd. CH - Švýcarsko Klíč. slova P92 steel ; welding ; creep damage ; creep fracture ; microstructure Vědní obor RIV JG - Hutnictví, kovové materiály Obor OECD Materials engineering CEP GA16-09518S GA ČR - Grantová agentura ČR Institucionální podpora UFM-A - RVO:68081723 EID SCOPUS 85038214376 DOI 10.4028/www.scientific.net/SSP.270.162 Anotace The microstructure and creep behaviour of the welded joints of P92 steel pipe were
investigated in order to determine the influence of orbital heat welding technology on the creep
resistance. Creep specimens were machined from the welded joints. Tensile creep tests of welded
joints were performed at 873 K using different stresses. The microstructure of tested specimens was
investigated by scanning electron microscope Tescan equipped with an electron-back scatter
diffraction. The creep results showed that the creep fracture strain of the welded joints decreases
with decreasing value of applied stress. Microstructure investigation showed that fracture behaviour
of welded joints is influenced by an enhanced cavity formation at grain boundaries in the heataffected
zone causing lower fracture ductility.Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2018