Crack Resistance Characterization in TiAl Intermetallics with Enhanced Toughness
- 1.
SYSNO ASEP 0480944 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název Crack Resistance Characterization in TiAl Intermetallics with Enhanced Toughness Tvůrce(i) Dlouhý, Ivo (UFM-A) RID, ORCID
Stratil, Luděk (UFM-A) ORCID
Fukutomi, H. (JP)
Hasegawa, M. (JP)Celkový počet autorů 4 Zdroj.dok. Analysis of Damage Features and Failures for Structural Materials and Parts. - Zürich : Trans Tech Publications Ltd, 2017 / Strnadel B. - ISSN 1013-9826 - ISBN 978-3-0357-1127-1 Rozsah stran s. 13-18 Poč.str. 6 s. Forma vydání Tištěná - P Akce 2016 - International Workshop on New Methods of Damage and Failure Analysis of Structural Parts /7./ Datum konání 01.11.2016 - 04.11.2016 Místo konání Yokohama Země JP - Japonsko Typ akce WRD Jazyk dok. eng - angličtina Země vyd. CH - Švýcarsko Klíč. slova Titanium aluminides ; Intermetallics ; Fracture micromechanisms ; Shear ligament toughening ; Fracture toughness ; Crack resistance Vědní obor RIV JG - Hutnictví, kovové materiály Obor OECD Materials engineering Institucionální podpora UFM-A - RVO:68081723 EID SCOPUS 85026896008 DOI 10.4028/www.scientific.net/KEM.741.13 Anotace The paper is focused on the analysis of the role of lamellar microstructure in fracture performance of model TiAl intermetallic compound. Coarse lamellar colonies and, at the same time, fine lamellar morphology were prepared by compressive deformation at 1553 K (region of stable alpha phase in TiAl equilibrium diagram) followed by controlled cooling to 1473 K (region of alpha+gamma phase) with delay on this temperature and then cooling down. The fracture toughness was evaluated by means of chevron notch technique. In addition, because of enhanced toughness, crack resistance curves were obtained by load - unload technique of pre-racked beams, namely in two directions of crack propagation relative to lamellar structure. Extensive development of shear ligament toughening mechanism was observed in fracture surfaces leading to quite good fracture toughness thanks to the heat treatment applied. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2018
Počet záznamů: 1