Physical simulation of the random failure of implanted braided NiTi stents
- 1.
SYSNO ASEP 0432500 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Physical simulation of the random failure of implanted braided NiTi stents Tvůrce(i) Hiřmanová, Klára (FZU-D)
Pilch, Jan (FZU-D) RID
Racek, Jan (FZU-D) RID, ORCID
Heller, Luděk (FZU-D) RID, ORCID
Šittner, Petr (FZU-D) RID, ORCID
Recman, L. (CZ)
Petrenec, M. (CZ)
Sedlák, Petr (UT-L) RID, ORCIDZdroj.dok. Journal of Materials Engineering and Performance. - : Springer - ISSN 1059-9495
Roč. 23, č. 7 (2014), s. 2650-2658Poč.str. 9 s. Akce International Conference on Shape Memory and Superelastic Technologies (SMST 2013) Datum konání 21.05.2013-24.05.2013 Místo konání Praha Země CZ - Česká republika Typ akce WRD Jazyk dok. eng - angličtina Země vyd. US - Spojené státy americké Klíč. slova electron microscopy ; failure analysis ; mechanical testing Vědní obor RIV BM - Fyzika pevných látek a magnetismus CEP GPP108/12/P111 GA ČR - Grantová agentura ČR GAP107/12/0800 GA ČR - Grantová agentura ČR 7E11058 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Institucionální podpora FZU-D - RVO:68378271 ; UT-L - RVO:61388998 UT WOS 000339010700053 EID SCOPUS 84904787401 DOI 10.1007/s11665-014-0916-9 Anotace A problem of random clinical failures of the braided esophageal NiTi stents has been addressed by performing physical simulation experiments on helical NiTi springs loaded in cyclic tension in air, water, and simulated biological fluid. Strains and stresses involved in spring deformation were analyzed through simulation by FEM implemented SMA model. It was found that the fatigue life of NiTi springs is significantly lower in fluids than in the air pointing toward the corrosion fatigue mechanism. There is, however, a fatigue limit roughly corresponding to the onset of martensitic transformation in the wire, which is not common for corrosion fatigue. It is proposed that surface TiO2 oxide cracking plays major role in that. Once the oxide layer on the NiTi wire surface fractures, typically during the first mechanical cycle, cracks in the oxide layer periodically open and close during subsequent mechanical cycling. Pracoviště Fyzikální ústav Kontakt Kristina Potocká, potocka@fzu.cz, Tel.: 220 318 579 Rok sběru 2015