High nitrogen and argon diffusion in cyclic olefin copolymer foil versus temperature
- 1.
SYSNO ASEP 0573701 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název High nitrogen and argon diffusion in cyclic olefin copolymer foil versus temperature Tvůrce(i) Cutroneo, Mariapompea (UJF-V) ORCID, RID, SAI
Silipigni, L. (IT)
Torrisi, A. (IT)
Macková, Anna (UJF-V) RID, ORCID, SAI
Malinský, Petr (UJF-V) RID, ORCID, SAI
Mikšová, Romana (UJF-V) RID, ORCID, SAI
Malý, J. (CZ)
Štofik, M. (CZ)
Slepička, P. (CZ)
Fajstavr, D. (CZ)
Holý, V. (CZ)
Dopita, M. (CZ)
Torrisi, L. (IT)Celkový počet autorů 13 Číslo článku 112195 Zdroj.dok. Vacuum. - : Elsevier - ISSN 0042-207X
Roč. 214, MAY (2023)Poč.str. 10 s. Forma vydání Tištěná - P Jazyk dok. eng - angličtina Země vyd. GB - Velká Británie Klíč. slova Cycle-olefin copolymer ; Diffusion coefficient ; Activation energy ; Nitrogen and argon diffusion Obor OECD Coating and films CEP EF16_013/0001812 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy GA22-10536S GA ČR - Grantová agentura ČR Výzkumná infrastruktura NanoEnviCz III - 90266 - Ústav fyzikální chemie J. Heyrovského AV ČR, v. v. i. Způsob publikování Omezený přístup Institucionální podpora UJF-V - RVO:61389005 UT WOS 001013388500001 EID SCOPUS 85160562350 DOI 10.1016/j.vacuum.2023.112195 Anotace Measurements of nitrogen and argon diffusion coefficient in cyclic olefin copolymer (COC) have been performed at different temperatures ranging between 21 & DEG,C and 101 & DEG,C. Optical transparent COC foils have been prepared with 10 & mu,m thickness and total surface of about 25 cm2. The foils have exhibited high purity in composition. The morphology of the COC surface has been investigated by Scanning Electron and Atomic Force Microscopies. The room temperature measured diffusion coefficients, of about 6.56 x 10-3 cm2/s and 6.30 x 10-3 cm2/s for N2 and Ar, respectively, have been obtained with a home-made experimental set-up by measuring the gas pressure gradient reduction applied to the two faces of COC thin foils versus the time. The foils show a significant increase of the N2 and Ar diffusion coefficients with the temperature. The native amorphous nature, the obtained nano-porous structure, the damage suffered by the thin foils of COC under high applied pressure are responsible of the evaluated high diffusion coefficients for nitrogen and argon gases. The experimental apparatus to measure the diffusion coefficients vs. temperature, the obtained results, the COC sheets microstructure, the measurements comparison with the literature data and possible COC applications in biomedicine are presented and discussed. Pracoviště Ústav jaderné fyziky Kontakt Markéta Sommerová, sommerova@ujf.cas.cz, Tel.: 266 173 228 Rok sběru 2024 Elektronická adresa https://doi.org/10.1016/j.vacuum.2023.112195
Počet záznamů: 1