Interfacial adhesion of thick NiTi coating on substrate stainless steel
- 1.
SYSNO ASEP 0566249 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Interfacial adhesion of thick NiTi coating on substrate stainless steel Tvůrce(i) Samal, Sneha Manjaree (FZU-D) ORCID, RID
Kopeček, Jaromír (FZU-D) RID, ORCID
Šittner, Petr (FZU-D) RID, ORCIDCelkový počet autorů 3 Číslo článku 8598 Zdroj.dok. Materials. - : MDPI
Roč. 15, č. 23 (2022)Poč.str. 16 s. Jazyk dok. eng - angličtina Země vyd. CH - Švýcarsko Klíč. slova NiTi ; thick layer ; plasma process ; stainless steel substrat Obor OECD Materials engineering CEP EF16_019/0000760 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy GA20-14114S GA ČR - Grantová agentura ČR LM2018110 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Způsob publikování Open access Institucionální podpora FZU-D - RVO:68378271 UT WOS 000897504100001 EID SCOPUS 85143792474 DOI 10.3390/ma15238598 Anotace Interfacial adhesion of thick NiTi coating on substrate stainless steel is investigated here.NiTi coating was deposited on the substrate by using the thermal plasma spraying method. Deposi tion of NiTi coating was carried out by using various levels of input power under an Ar atmosphere. Multiple coating layers were deposited on the stainless steel surface for a specific thickness. The cross-section of the plasma-sprayed samples were prepared and characterized by using various techniques. The hardness of the coating layers on the surface and cross-section was examined. The thickness of the coating increased with the increase in power. No cracks were detected in the interface for the NiTi coating deposited at 12 kW power. However minor pores were observed at some regions along the interface at the sample prepared at 9 kW power. Pracoviště Fyzikální ústav Kontakt Kristina Potocká, potocka@fzu.cz, Tel.: 220 318 579 Rok sběru 2023 Elektronická adresa https://hdl.handle.net/11104/0337636
Počet záznamů: 1