Direct comparison between Co-28Cr-6Mo alloy prepared by selective laser melting and traditional investment casting
- 1.
SYSNO ASEP 0546270 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název Direct comparison between Co-28Cr-6Mo alloy prepared by selective laser melting and traditional investment casting Tvůrce(i) Roudnická, Michaela (FZU-D) ORCID
Bigas, J. (CZ)
Šreibr, V. (CZ)
Paloušek, D. (CZ)
Vojtěch, D. (CZ)Celkový počet autorů 5 Číslo článku 012046 Zdroj.dok. IOP Conference Series: Materials Science and Engineering, 1178. - Bristol : IOP Publishing Ltd, 2021 - ISSN 1757-8981 Poč.str. 6 s. Forma vydání Tištěná - P Akce International Conference on Recent Trends in Structural Materials (COMAT 2020) /6./ Datum konání 30.09.2020 - 04.10.2020 Místo konání Plzeň Země CZ - Česká republika Typ akce WRD Jazyk dok. eng - angličtina Země vyd. GB - Velká Británie Klíč. slova Co-28Cr-6Mo ; selective Laser Melting ; investment casting ; microstructure ; mechanical properties Vědní obor RIV BM - Fyzika pevných látek a magnetismus Obor OECD Condensed matter physics (including formerly solid state physics, supercond.) Institucionální podpora FZU-D - RVO:68378271 DOI 10.1088/1757-899X/1178/1/012046 Anotace In this contribution, we bring a direct comparison between the microstructures and mechanical properties of Co-28Cr-6Mo alloy prepared by SLM and investment casting. Due to significant differences in microstructure fineness and phase composition, SLM is revealed to increase not only material strength and hardness but concurrently plasticity. As a result of rapid solidification during SLM, very fine cellular microstructure with Mo microsegregation at cell walls is formed without the occurrence of any secondary phases. The distinctive microstructure of the additively manufactured alloy can be expected to be the cause of many other variances in the material behaviour. Pracoviště Fyzikální ústav Kontakt Kristina Potocká, potocka@fzu.cz, Tel.: 220 318 579 Rok sběru 2022 Elektronická adresa https://iopscience.iop.org/article/10.1088/1757-899X/1178/1/012046/pdf
Počet záznamů: 1