Development of advanced Fe–Al–O ODS alloy\nmicrostructure and properties due to heat treatment
- 1.
SYSNO ASEP 0534784 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Development of advanced Fe–Al–O ODS alloy
microstructure and properties due to heat treatmentTvůrce(i) Fintová, Stanislava (UFM-A) ORCID
Kuběna, Ivo (UFM-A) RID, ORCID
Luptáková, Natália (UFM-A) RID, ORCID
Jarý, Milan (UFM-A)
Šmíd, Miroslav (UFM-A) RID, ORCID
Stratil, Luděk (UFM-A) ORCID
Šiška, Filip (UFM-A) RID, ORCID
Svoboda, Jiří (UFM-A) RID, ORCIDCelkový počet autorů 8 Zdroj.dok. Journal of Materials Research. - : Springer - ISSN 0884-2914
Roč. 35, č. 20 (2020), s. 2789-2797Poč.str. 9 s. Jazyk dok. eng - angličtina Země vyd. US - Spojené státy americké Klíč. slova microstructure ; mechanical alloying ; scanning electron microscopy (SEM) Vědní obor RIV JG - Hutnictví, kovové materiály Obor OECD Materials engineering CEP LQ1601 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Způsob publikování Omezený přístup Institucionální podpora UFM-A - RVO:68081723 UT WOS 000595594900015 EID SCOPUS 85094947750 DOI 10.1557/jmr.2020.278 Anotace Fe–Al–O ODS alloy prepared via mechanical alloying was subjected to three different heat treatments. Material
basic state exhibited a fine-grained (300–500 nm) microstructure with fine dispersion of aluminum oxide particles
(60% up to 20 nm). Heat treatment at 1100 °C for 3 h resulted in local grain and particles coarsening.
Prolongation of the heat treatment to 24 h resulted in further grain (50 % up to 5 μm) and particle (25 % with
size 25–40 nm) coarsening. Annealing at 1200 °C for 24 h led to a bimodal microstructure (35 % of grains with
size 100–250 μm and 45 % of particles with size 30–60 nm) and substantial oxide particle coarsening.
Microstructural changes resulted in tensile strength decrease and ductility increase. Tensile tests at 800 °C
revealed a 90% decrease of tensile strength while ductility increased 4–6 times when compared to the room
temperature tests. The hardening ratio was below 10 % for all the alloys and both test temperatures.Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2021 Elektronická adresa https://www.cambridge.org/core/journals/journal-of-materials-research/article/abs/development-of-advanced-fealo-ods-alloy-microstructure-and-properties-due-to-heat-treatment/A3DE7A6CED71C31F834E96316FFAA7B9