Interaction of Creep and High Cycle Fatigue of IN 713LC Superalloy
- 1.
SYSNO ASEP 0480264 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název Interaction of Creep and High Cycle Fatigue of IN 713LC Superalloy Tvůrce(i) Horník, V. (CZ)
Šmíd, Miroslav (UFM-A) RID, ORCID
Hutař, Pavel (UFM-A) RID, ORCID
Kunz, Ludvík (UFM-A) RID, ORCID
Hrbáček, K. (CZ)Celkový počet autorů 5 Zdroj.dok. Materials Structure & Micromechanics of Fracture VIII. - Zürrich : Trans Tech Publications, 2017 / Šandera P. - ISSN 1662-9779 - ISBN 978-3-03835-626-4 Rozsah stran s. 595-598 Poč.str. 4 s. Forma vydání Tištěná - P Akce MSMF8. International Conference on Materials Structure and Micromechanics of Fracture /8./ Datum konání 27.06.2016 - 29.06.2016 Místo konání Brno Země CZ - Česká republika Typ akce WRD Jazyk dok. eng - angličtina Země vyd. CH - Švýcarsko Klíč. slova Creep-fatigue interaction ; Fractography ; High temperature ; IN 713LC ; Superalloy Vědní obor RIV JL - Únava materiálu a lomová mechanika Obor OECD Audio engineering, reliability analysis CEP TA04011525 GA TA ČR - Technologická agentura ČR LM2015069 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Institucionální podpora UFM-A - RVO:68081723 EID SCOPUS 85009830512 DOI 10.4028/www.scientific.net/SSP.258.595 Anotace The study deals with the interaction of creep and high cycle fatigue of cast polycrystalline nickel-based superalloy IN 713LC at high temperatures. Previous works indicated that creep lifetime of superalloy structures was un-affected or even slightly increased in the cases with superimposed vibrations. The reason for this behaviour was not well described up to now. Therefore, set of fatigue tests was conducted at high mean stresses level to observe this phenomenon. The mean stress was kept constant while the stress amplitudes were selected in order to measure wide range of conditions from pure creep to pure fatigue. Fractographic analysis by scanning electron microscopy (SEM) was done with the aim to identify governing damage mechanisms for particular test conditions as a preliminary evaluation of conducted tests. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2018
Počet záznamů: 1