Effect of thermal barrier coating on low cycle fatigue behavior of cast Inconel 713LC at 900 °C
- 1.
SYSNO ASEP 0435378 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název Effect of thermal barrier coating on low cycle fatigue behavior of cast Inconel 713LC at 900 °C Tvůrce(i) Obrtlík, Karel (UFM-A) RID, ORCID
Hutařová, S. (CZ)
Čelko, L. (CZ)
Juliš, M. (CZ)
Podrábský, T. (CZ)
Šulák, Ivo (UFM-A) ORCIDCelkový počet autorů 6 Zdroj.dok. 11th International Fatigue Congress. - Zurich : Trans Tech Publications, 2014 / Clark G. ; Wang Ch. - ISSN 1022-6680 - ISBN 978-3-03835-008-8 Rozsah stran s. 848-853 Poč.str. 6 s. Forma vydání Online - E Akce Fatigue 2014 - International Fatigue Congress /11./ Datum konání 02.03.2014-07.03.2014 Místo konání Melbourne Země AU - Austrálie Typ akce WRD Jazyk dok. eng - angličtina Země vyd. CH - Švýcarsko Klíč. slova High temperature fatigue ; TBC ; Inconel 713LC ; Fatigue life Vědní obor RIV JL - Únava materiálu a lomová mechanika CEP GAP107/11/2065 GA ČR - Grantová agentura ČR FR-TI4/030 GA MPO - Ministerstvo průmyslu a obchodu Institucionální podpora UFM-A - RVO:68081723 UT WOS 000337767700132 DOI 10.4028/www.scientific.net/AMR.891-892.848 Anotace The effect of thermal barrier coating (TBC) on low cycle fatigue behavior of cast superalloy Inconel 713 LC has been studied at 900 °C. The TBC consisting of a CoNiCrAlY bond coat and a zirconia (ZrO2) top coat stabilized by 8% yttria (Y2O3) was deposited on the gauge section of cylindrical specimens using the atmospheric plasma spray technique. Cylindrical specimens of Inconel 713LC in as-received condition and with surface treatment were cyclically strained under strain control with constant total strain amplitude in symmetrical cycle at 900 °C in air. Hardening/softening curves, cyclic stress-strain curve and fatigue life data of coated and uncoated material were obtained. The stress response of the TBC coated specimens is lower in comparison with the uncoated specimens. Detrimental effect of surface treatment on the Basquin curve is documented. Specimen sectioning and fracture surface observations revealed fatigue damage mechanisms and help to discuss differences in fatigue behavior of the coated and uncoated superalloy. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2015
Počet záznamů: 1