Post polymerisation hypercrosslinking of styrene/divinylbenzene poly(HIPE)s: creating micropores within macroporous polymer
- 1.
SYSNO ASEP 0424542 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Post polymerisation hypercrosslinking of styrene/divinylbenzene poly(HIPE)s: creating micropores within macroporous polymer Tvůrce(i) Sevšek, U. (SI)
Brus, Jiří (UMCH-V) RID, ORCID
Jeřábek, Karel (UCHP-M) RID, ORCID, SAI
Krajnc, P. (SI)Zdroj.dok. Polymer. - : Elsevier - ISSN 0032-3861
Roč. 55, č. 1 (2014), s. 410-415Poč.str. 6 s. Jazyk dok. eng - angličtina Země vyd. GB - Velká Británie Klíč. slova polyHIPE ; hypercrosslinking ; porous polymers Vědní obor RIV JI - Kompozitní materiály Vědní obor RIV – spolupráce Ústav chemických procesů - Průmyslová chemie a chemické inženýrství CEP GA13-29009S GA ČR - Grantová agentura ČR Institucionální podpora UMCH-V - RVO:61389013 ; UCHP-M - RVO:67985858 UT WOS 000330207100052 EID SCOPUS 84891826627 DOI 10.1016/j.polymer.2013.09.026 Anotace Porous copolymers of styrene and divinylbenzene (DVB) were prepared by emulsion templating using high internal phase emulsions (HIPEs) as precursors for monoliths. The ratio of monomers was varied in order to obtain samples with different degrees of crosslinking and different amounts of unreacted vinyl groups originating from DVB. PolyHIPE monoliths were subjected to reswelling and treatment with a radical initiator. Significant enlargement of the amount of meso- and micropores in the material was found resulting in a substantial increase of BET surface area, up to 7.2 times compared to untreated polyHIPEs. The treated PolyHIPE monoliths retained the open macroporous morphology typical of polyHIPE materials. Solid state 13C NMR experiments were used to determine the amount of unreacted vinyl groups in polyHIPE samples, both before and after the hypercrosslinking treatment. Pracoviště Ústav makromolekulární chemie Kontakt Eva Čechová, cechova@imc.cas.cz ; Tel.: 296 809 358 Rok sběru 2014
Počet záznamů: 1