Influence of Hold Times on Fatigue Life and Fracture Behavior of Cast Superalloy INCONEL 713LC at 700°C
- 1.
SYSNO ASEP 0332380 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV Záznam nebyl označen do RIV Název Influence of Hold Times on Fatigue Life and Fracture Behavior of Cast Superalloy INCONEL 713LC at 700°C Tvůrce(i) Obrtlík, Karel (UFM-A) RID, ORCID
Man, Jiří (UFM-A) RID, ORCID
Petrenec, Martin (UFM-A)
Polák, Jaroslav (UFM-A) RID, ORCID
Podrábský, T. (CZ)Celkový počet autorů 5 Zdroj.dok. Proceedings of 12th International Conference on Fracture. - Ottawa : NRCan - CANMET, 2009 - ISBN N Rozsah stran s. 1-9 Poč.str. 9 s. Forma vydání CD-ROM - CD-ROM Akce International Conference on Fracture /12./ Datum konání 12.07.2009-17.07.2009 Místo konání Ottawa Země CA - Kanada Typ akce WRD Jazyk dok. eng - angličtina Země vyd. CA - Kanada Klíč. slova Fatigue life ; Hold times ; High temperature ; Inconel 713LC Vědní obor RIV JL - Únava materiálu a lomová mechanika CEP 1QS200410502 GA AV ČR - Akademie věd GA106/08/1631 GA ČR - Grantová agentura ČR GA106/07/1507 GA ČR - Grantová agentura ČR CEZ AV0Z20410507 - UFM-A (2005-2011) Anotace Influence of tensile strain holds on fatigue life and fracture behavior in cast nickel-based superalloy INCONEL 713 LC was studied under symmetrical total strain cycling at 700 °C in air. Structure of the superalloy is documented. Continuous cycling and cycling with 10 min dwell in the tensile tip of the hysteresis loop were applied to cylindrical specimens. Surface topography, fracture surface and specimen sections were observed in SEM. Fatigue life in Manson-Coffin and Basquin representation in cycling with dwells is reduced in comparison with continuous cycling. Pure fatigue and pure creep data are used to analyze the fatigue damage with dwells. Surface relief and fracture surface observations reveal the change in damage mechanisms with the introduction of dwells. Density of slip markings in cycling with dwells decreases in comparison with continuous cycling. The life reduction due to dwells is discussed with respect to fatigue interaction with creep and environment. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2010
Počet záznamů: 1