Fracture Toughness and Fracture Mechanisms in TiAl Based Intermetalics
- 1.
SYSNO ASEP 0321143 Druh ASEP K - Konferenční příspěvek (lokální konf.) Zařazení RIV Stať ve sborníku Název Fracture Toughness and Fracture Mechanisms in TiAl Based Intermetalics Překlad názvu Lomová houževnatost a mechanismy porušování intermetalika na bázi TiAl Tvůrce(i) Dlouhý, Ivo (UFM-A) RID, ORCID
Chlup, Zdeněk (UFM-A) RID, ORCID
Hadraba, Hynek (UFM-A) RID, ORCID
Kozák, Vladislav (UFM-A) RID, ORCIDZdroj.dok. New Methods of Damage and Failure Analysis of Structural Parts. - Ostrava : VŠB - TU Ostrava, 2008 - ISBN 978-80-248-1813-9
S. 235-243Poč.str. 8 s. Akce New Methods of Damage and Failure Analysis of Structural Parts Datum konání 08.09.2008-12.09.2008 Místo konání Ostrava Země CZ - Česká republika Typ akce WRD Jazyk dok. eng - angličtina Země vyd. CZ - Česká republika Klíč. slova TiAl ; intermetalics ; fracture toughness ; micromechanisms of fracture ; shear ligament toughening Vědní obor RIV JG - Hutnictví, kovové materiály CEP GA106/07/0762 GA ČR - Grantová agentura ČR CEZ AV0Z20410507 - UFM-A (2005-2011) Anotace The paper is focused on the analysis of the role of microstructure in fracture performance of TiAl intermetalics at room and elevated temperatures. Tensile properties, flexural strength and fracture toughness have been evaluated for Ti-40Al-2Cr-2Nb-1B and Ti-46Al-0,7Cr-0,1Si-7Nb-0,2Ni alloys. Positive Nb effect on fracture resistance was found; fracture toughness of the high Nb alloy was increased at contemporary increase of tensile and flexural strength. Fracture surfaces were evaluated using scanning electron microscopy showing the key role of mechanical twinning in deformation of both alloys. As a governing mechanism of the crack initiation a microcrack nucleation at boundaries between -TiAl grains was confirmed. Based on findings obtained key aspects of the effect of separate microstructural components have been discussed. Summary of toughening effects acting in this group of intermetalics has been provided. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2009
Počet záznamů: 1