Growth, structure, spectroscopy, and laser operation of a “Mixed” Yb (Y,Lu).sub.3./sub.Al.sub.5./sub.O.sub.12./sub. garnet crystal

Slimi, S.; Loiko, P.; Pan, M.; Lehoux, P.; Jambunathan, Venkatesan; Smrž, Martin; Mocek, Tomáš; Wang, Y.; Chen, W.; Petrov, V.; Solé, R.M.; Aguiló, M.; Díaz, F.; Camy, P.; Mateos, X.

doi:https://dx.doi.org/10.3390/cryst13111588

Počet záznamů: 1

Growth, structure, spectroscopy, and laser operation of a “Mixed” Yb (Y,Lu).sub.3./sub.Al.sub.5./sub.O.sub.12./sub. garnet crystal

1.

SYSNO ASEP	0579752
Druh ASEP	J - Článek v odborném periodiku
Zařazení RIV	J - Článek v odborném periodiku
Poddruh J	Článek ve WOS
Název	Growth, structure, spectroscopy, and laser operation of a “Mixed” Yb (Y,Lu)₃Al₅O₁₂ garnet crystal
Tvůrce(i)	Slimi, S. (ES) Loiko, P. (FR) Pan, M. (CN) Lehoux, P. (FR) Jambunathan, Venkatesan (FZU-D) Smrž, Martin (FZU-D)_{RID, ORCID} Mocek, Tomáš (FZU-D)_{RID, ORCID, SAI} Wang, Y. (DE) Chen, W. (CN) Petrov, V. (DE) Solé, R.M. (ES) Aguiló, M. (ES) Díaz, F. (ES) Camy, P. (FR) Mateos, X. (ES)
Celkový počet autorů	15
Číslo článku	1588
Zdroj.dok.	Crystals. - : MDPI - ISSN 2073-4352 Roč. 13, Nov (2023)
Poč.str.	18 s.
Jazyk dok.	eng - angličtina
Země vyd.	CH - Švýcarsko
Klíč. slova	garnet crystals ; ytterbium ion ; crystal structure ; optical spectroscopy ; solid-state lasers
Vědní obor RIV	BH - Optika, masery a lasery
Obor OECD	Optics (including laser optics and quantum optics)
CEP	EF15_006/0000674 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy
Způsob publikování	Open access
Institucionální podpora	FZU-D - RVO:68378271
UT WOS	001122510200001
EID SCOPUS	85178130832
DOI	https://doi.org/10.3390/cryst13111588
Anotace	A single crystal of ytterbium-doped “mixed” yttrium–lutetium aluminum garnet with a stoichiometric composition of (Y0.601Lu0.233Yb0.166)3Al5O12 was grown by the Czochralski method and its structure, vibronic, spectroscopic, and laser properties were studied. The stimulated-emission cross-section for Yb3+ ions was maximized to 2.53 × 10−20 cm2 at 1031 nm. The emission bandwidth was ~8 nm, and the reabsorption-free luminescence lifetime of the 2F5/2 state was 1.063 ms. Pumped at 941 nm, the Yb laser generated a maximum output power of 1.04 W at 1.03 and 1.05 µm with a high slope efficiency of 76.4% and a laser threshold of 76 mW. A continuous wavelength tuning over a range of 51.6 nm (1026.4–1078.0 nm) was also achieved. Power scaling was achieved using a 969 nm diode-pumped microchip cavity. A maximum output power of ~9 W was obtained at 1.05 µm with a slope efficiency of 76% and an almost circular laser beam profile.