Effect of residual stresses to the crack path in alumina/zirconia laminates
- 1.
SYSNO ASEP 0531649 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Effect of residual stresses to the crack path in alumina/zirconia laminates Tvůrce(i) Chlup, Zdeněk (UFM-A) RID, ORCID
Novotná, L. (CZ)
Šiška, Filip (UFM-A) RID, ORCID
Drdlík, D. (CZ)
Hadraba, Hynek (UFM-A) RID, ORCIDCelkový počet autorů 5 Zdroj.dok. Journal of the European Ceramic Society. - : Elsevier - ISSN 0955-2219
Roč. 40, č. 15 (2020), s. 5810-5818Poč.str. 9 s. Jazyk dok. eng - angličtina Země vyd. GB - Velká Británie Klíč. slova Laminates ; Alumina ; Zirconia ; Residual/internal stresses ; Crack path Vědní obor RIV JH - Keramika, žáruvzdorné materiály a skla Obor OECD Ceramics CEP GA17-08153S GA ČR - Grantová agentura ČR LQ1601 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Způsob publikování Omezený přístup Institucionální podpora UFM-A - RVO:68081723 UT WOS 000564730300001 EID SCOPUS 85087084006 DOI 10.1016/j.jeurceramsoc.2020.06.044 Anotace Laminates with alternating layers are well known from nature. The strongly bonded alumina/zirconia (Al2O3/
ZrO2) layers can combine high fracture resistance with high strength and stiffness when properly tailored. The
presence of compressive residual stresses formed in Al2O3 layers can suppress and deflect cracks propagating
through the layers. The crack path is governed by both the elastic properties and the internal stress field of
individual layers. The laminates with various layer-thickness ratios ranging from 0.1 to 3 were used to investigate
the effect of residual stresses and influence of crack formation pattern on the crack path development.
The indentation surface cracks observed in various alumina-zirconia laminates exhibit the same crack deflection
independently on the level of internal stresses. The crack deflection observed on the fracture surfaces of bending
specimens was related to the indentations cracks. The complicated crack path was explained experimentally by
3D reconstruction with the support of numerical simulations.Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2021 Elektronická adresa https://www.sciencedirect.com/science/article/pii/S0955221920305148?via%3Dihub