Creep behaviour and superplasticity in UFG Ti-6Al-4V alloy
- 1.
SYSNO ASEP 0450341 Druh ASEP A - Abstrakt Zařazení RIV Není vybrán druh dokumentu Název Creep behaviour and superplasticity in UFG Ti-6Al-4V alloy Tvůrce(i) Král, Petr (UFM-A) RID, ORCID
Dvořák, Jiří (UFM-A) RID, ORCID
Kudrjavtsev, E. (RU)
Zherebtsov, S. (RU)
Salishchev, G. A. (RU)
Kvapilová, Marie (UFM-A) RID, ORCID
Sklenička, Václav (UFM-A) RID, ORCIDCelkový počet autorů 7 Zdroj.dok. Book of Abstracts. 17th International Conference on the Strength of Materials (ICSMA-17). - Brno : Ústav fyziky materiálů AV ČR, v. v. i., 2015 / Dlouhý A. ; Kunz L. - ISBN 978-80-87434-07-9
S. 230-230Poč.str. 1 s. Forma vydání Tištěná - P Akce ICSMA-17 International Conference on the Strength of Materials /17./ Datum konání 09.08.2015-14.08.2015 Místo konání Brno Země CZ - Česká republika Typ akce WRD Jazyk dok. eng - angličtina Země vyd. CZ - Česká republika Klíč. slova creep behaviour ; superplasticity ; microstructure ; ultrafine-grained alloy Vědní obor RIV JJ - Ostatní materiály Institucionální podpora UFM-A - RVO:68081723 Anotace In this paper, the creep behaviour of a Ti-6Al-4V alloy processed by multiaxial forging was investigated. The originally as-received coarse –grained titanium alloy was processed by multiaxial forging in the temperature range from 973 to 748 K. The initial strain rate was 10-3 s-1 strain per deformation step was about 0.5. Ultrafine-grained Ti alloy with mean grain size d~150 nm was tested at 648-873 K at constant stress in compression and under constant load in tension. The values of the stress exponent of the minimum creep rate n and creep activation energy Qc were determined. The microstructure of specimens after creep testing was examined by FIB/SEM Tescan Lyra 3 equipped with NordlysNano EBSD detector operating at an accelerating voltage of 20 kV with specimen tilted at 70°. The EBSD analyses of both gauge length and head of specimens were performed in the longitudinal sections parallel to the stress direction. The results of the uniaxial creep tests showed different values of the stress exponents of the minimum creep rate n at 673 K and 873 K. The values of creep activation energy Qc indicated the change of creep deformation mechanism above 773 K. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2016
Počet záznamů: 1