Emanation thermal analysis study of the preparation of ruthenia-titania-based finely dispersed powders
- 1.0163381 - UACH-T 20023055 RIV US eng J - Článek v odborném periodiku
Balek, V. - Mitsuhashi, T. - Zeleňák, V. - Večerníková, Eva - Šubrt, Jan - Haneda, H. - Bezdička, Petr
Emanation thermal analysis study of the preparation of ruthenia-titania-based finely dispersed powders.
Journal of Colloid and Interface Science. Roč. 248, č. 1 (2002), s. 47-53. ISSN 0021-9797. E-ISSN 1095-7103
Výzkumný záměr: CEZ:AV0Z4032918
Klíčová slova: emanation thermal analysis * TiO2 * RuO2
Kód oboru RIV: CA - Anorganická chemie
Impakt faktor: 1.466, rok: 2002
Emanation thermal analysis (ETA), thermogravimetry (TG), differential thermal analysis (DTA), X-ray diffraction analysis (XRD), and transmission electron microscopy (TEM) were used for the characterization of thermal behavior of hydrous oxides (RuO2)(x)-(TiO2)(1-x) (.) nH(2)O and dehydrated oxides (RuO2)(x)-(TiO2)(1-x), respectively (x =1, 0.9, and 0.7) on heating in argon and argon + 10% hydrogen, respectively. The samples were heated in the range 20-600degreesC at the constant heating rate 6 K/min. From the TG and DTA results the temperature intervals of dehydration and/or reduction of ruthenium dioxide into Ru metal were determined. ETA (based on the measurement of radon previously incorporated into the sample) brought about the information about surface area development and microstructure changes in the near surface layers up to 80 mm under in situ conditions of the heating. The temperature intervals of the annealing of near surface and structure defects serving as diffusion paths for radon were determined from the ETA results.