Failure behaviour of cladding made from Sv 07Kh25N13 austenitic stainless steel
- 1.
SYSNO ASEP 0536631 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Failure behaviour of cladding made from Sv 07Kh25N13 austenitic stainless steel Tvůrce(i) Štefan, Jan (UT-L)
Siegl, J. (CZ)
Adámek, J. (CZ)
Kopřiva, R. (CZ)
Kytka, M. (CZ)Celkový počet autorů 5 Číslo článku 104275 Zdroj.dok. International Journal of Pressure Vessels and Piping. - : Elsevier - ISSN 0308-0161
Roč. 189, February (2021)Poč.str. 7 s. Forma vydání Tištěná - P Jazyk dok. eng - angličtina Země vyd. GB - Velká Británie Klíč. slova nuclear reactor pressure vessel ; austenitic cladding ; fracture toughness testing ; fractography ; metallography Vědní obor RIV JL - Únava materiálu a lomová mechanika Obor OECD Applied mechanics CEP EF15_003/0000493 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Způsob publikování Omezený přístup Institucionální podpora UT-L - RVO:61388998 UT WOS 000614145400017 EID SCOPUS 85097455003 DOI 10.1016/j.ijpvp.2020.104275 Anotace Sv 07Kh25N13 is austenitic stainless steel used in nuclear industry. Due to its excellent corrosion resistance in the environment of WWER type nuclear reactor primary circuit, it is applied as anticorrosive cladding of the reactor pressure vessel. In this paper, results of detailed experimental research of failure behaviour of the cladding are presented. Static fracture toughness values J0.2 exhibited an extreme scatter. Metallographic analysis performed on the fractured specimens revealed large variations of structure within every single cladding layer. Fractographic analysis performed on fracture surfaces revealed considerable variations of micromechanisms taking place during ductile crack propagation. Conclusions on the relationship between the local microstructure, the failure mode and the fracture toughness of the cladding were drawn. Results indicate that the fracture toughness of the cladding was primarily determined by local amount of sigma phase in the area of crack propagation. Pracoviště Ústav termomechaniky Kontakt Marie Kajprová, kajprova@it.cas.cz, Tel.: 266 053 154 ; Jana Lahovská, jaja@it.cas.cz, Tel.: 266 053 823 Rok sběru 2022 Elektronická adresa https://www.sciencedirect.com/science/article/pii/S0308016120302507
Počet záznamů: 1