Quantification of microstructural changes in limestone cement paste stored in sulfate environment at low temperature
- 1.
SYSNO ASEP 0532112 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název Quantification of microstructural changes in limestone cement paste stored in sulfate environment at low temperature Tvůrce(i) Sotiriadis, Konstantinos (UTAM-F) RID, ORCID, SAI
Hlobil, Michal (UTAM-F) RID, SAI, ORCID
Machová, Dita (UTAM-F) RID, ORCID, SAI
Mácová, Petra (UTAM-F) RID, SAI, ORCID
Viani, Alberto (UTAM-F) RID, ORCID, SAI
Vopálenský, Michal (UTAM-F) RID, ORCID, SAICelkový počet autorů 6 Zdroj.dok. Solid State Phenomena, 26th International Conference Concrete Days, 309. - Baech : Trans Tech Publications, 2020 / Nenadálová Š. ; Johová P. - ISSN 1012-0394 - ISBN 978-3-0357-1668-9 Rozsah stran s. 3-7 Poč.str. 5 s. Forma vydání Tištěná - P Akce International Conference Concrete Days /26./ Datum konání 20.11.2019 - 21.11.2019 Místo konání Hradec Králové Země CZ - Česká republika Typ akce EUR Jazyk dok. eng - angličtina Země vyd. CH - Švýcarsko Klíč. slova limestone cement ; sulfates ; microstructure ; X-ray tomography Vědní obor RIV JN - Stavebnictví Obor OECD Materials engineering CEP GJ18-26056Y GA ČR - Grantová agentura ČR Způsob publikování Omezený přístup Institucionální podpora UTAM-F - RVO:68378297 EID SCOPUS 85090294025 DOI 10.4028/www.scientific.net/SSP.309.3 Anotace Portland-limestone cement paste specimens were stored in magnesium sulfate solution at 5°C for 6 months, the occurring microstructural changes have been monitored on a monthly basis. Extent of deterioration was quantitatively assessed with different techniques. The X-ray microcomputed tomography was employed to describe non-invasively the pore structure and extend of deterioration. X-ray powder diffraction and infrared spectroscopy were used to characterize the phase changes occurred in the course of the sulfate attack. Compressive strength tests reflected the effect of the process on mechanical performance. The results indicate the rapid degradation of the system, owing, mainly, to crack formation, expansion, and finally loss of cohesion between the deteriorated parts of the specimens and the sound cement matrix, as a consequence of the formation of new phases. The progress of an irregular deterioration front was observed. The presence of complex phases (thaumasite, ettringite) was proved, however, the deteriorated parts of the specimens mostly consisted of gypsum. Pracoviště Ústav teoretické a aplikované mechaniky Kontakt Kulawiecová Kateřina, kulawiecova@itam.cas.cz, Tel.: 225 443 285 Rok sběru 2021 Elektronická adresa https://doi.org/10.4028/www.scientific.net/SSP.309.3
Počet záznamů: 1