Very high cycle fatigue tests of high strength steels S355 J0 and S355 J2

0509517 - ÚFM 2020 RIV NL eng C - Konferenční příspěvek (zahraniční konf.)
Klusák, Jan - Seitl, Stanislav
Very high cycle fatigue tests of high strength steels S355 J0 and S355 J2.
ICSI 2019 The 3rd International Conference on Structural Integrity. Amsterdam: Elsevier, 2019 - (Moreira, P.; Tavares, P.), s. 576-581. Procedia Structural Integrity, 17. ISSN 2452-3216.
[ICSI 2019 - International Conference on Structural Integrity /3./. Madeira (PT), 02.09.2019-05.09.2019]
Grant CEP: GA MŠMT(CZ) LQ1601; GA ČR GA17-01589S
Institucionální podpora: RVO:68081723
Klíčová slova: Very high cycle fatigue * high strength steel * fatigue life * structural steel
Obor OECD: Audio engineering, reliability analysis

The high strength steel S355 is frequently used in civil engineering to design bridges, its elements or simple engineering parts. The properties of the steellead to savings both material’s and economical meeting strict construction requirements. From this reason, fatigue resistance of the material is in focus of researchers. Results obtained from experimental observations provide reliable inputs to lifetime assessments and numerical simulations of fatigue loaded structures like bridges, cranes and other constructions. As these constructions are designed for a long life, we have studied the properties of the material in the field of high-cycle and very high-cycle fatigue. Tests of two standard S355 J0 and S355 J2 steel grades were performed on ultrasonic fatigue testing system. Both steels exhibited fatigue behavior in gigacycle region while S355 J2 exhibited higher number of cycles to failure. Fracture surfaces were studied and showed both surface and subsurface crack initiation.