Aluminum Wire Meshes Coated with Co-Mn-Al and Co Oxides as Catalysts for Deep Ethanol Oxidation.
- 1.
SYSNO ASEP 0486085 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Aluminum Wire Meshes Coated with Co-Mn-Al and Co Oxides as Catalysts for Deep Ethanol Oxidation. Tvůrce(i) Jirátová, Květa (UCHP-M) RID, ORCID, SAI
Kovanda, F. (CZ)
Balabánová, Jana (UCHP-M) RID, ORCID, SAI
Kšírová, P. (CZ)Zdroj.dok. Catalysis Today. - : Elsevier - ISSN 0920-5861
Roč. 304, SI (2018), s. 165-171Poč.str. 7 s. Akce Czech-Italian-Spanish Symposium in Catalysis /7./ Datum konání 13.06.2017 - 17.06.2017 Místo konání Třešť Země CZ - Česká republika Typ akce EUR Jazyk dok. eng - angličtina Země vyd. NL - Nizozemsko Klíč. slova GA17-08389S ; Co-Mn-Al mixed oxides ; aluminum mesh Vědní obor RIV CI - Průmyslová chemie a chemické inženýrství Obor OECD Chemical process engineering CEP GA17-08389S GA ČR - Grantová agentura ČR Institucionální podpora UCHP-M - RVO:67985858 UT WOS 000425179000021 EID SCOPUS 85030482361 DOI 10.1016/j.cattod.2017.09.046 Anotace Aluminum meshes with different wire diameter and open space area were anodized in H2SO4 solution and then treated under hydrothermal conditions in aqueous solution of Co and Mn nitrates. The layered double hydroxide precursors formed on the supports surface were transformed into Co-Mn-Al mixed oxides after heating. For comparison, aluminum mesh coated with Co3O4 oxide was also prepared. Activity of the catalysts depended on the amount of active components deposited on the mesh. Comparison of specific activities at the same space velocity demonstrated the size of mixed oxides particles as the important parameter for oxidation activity: decreasing in particle size led to increased catalysts efficiency. The Co3O4 oxide deposited from Co(OH)2 suspension provided more active catalyst than Co-Mn-Al mixed oxides obtained by long-term hydrothermal treatment of the anodized aluminum meshes followed by heating. Pracoviště Ústav chemických procesů Kontakt Eva Jirsová, jirsova@icpf.cas.cz, Tel.: 220 390 227 Rok sběru 2019
Počet záznamů: 1