Stage I fatigue cracking in MAR-M 247 superalloy at elevated temperatures
- 1.
SYSNO ASEP 0465127 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název Stage I fatigue cracking in MAR-M 247 superalloy at elevated temperatures Tvůrce(i) Šmíd, Miroslav (UFM-A) RID, ORCID
Hutař, Pavel (UFM-A) RID, ORCID
Horník, V. (CZ)
Hrbáček, K. (CZ)
Kunz, Ludvík (UFM-A) RID, ORCIDCelkový počet autorů 5 Zdroj.dok. 21st European Conference on Fracture. - Amsterdam : Elsevier, 2016 - ISSN 2452-3216 Rozsah stran 3018–3025, s. 3018-3025 Poč.str. 8 s. Forma vydání Online - E Akce ECF21 - European Conference on Fracture /21./ Datum konání 20.06.2016-24.06.2016 Místo konání Catania Země IT - Itálie Typ akce WRD Jazyk dok. eng - angličtina Země vyd. NL - Nizozemsko Klíč. slova Superalloy ; High cycle fatigue ; Elevated temperature ; MAR-M 247 ; Fatigue crack initiation Vědní obor RIV JL - Únava materiálu a lomová mechanika Obor OECD Audio engineering, reliability analysis CEP TA04011525 GA TA ČR - Technologická agentura ČR ED1.1.00/02.0068 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Institucionální podpora UFM-A - RVO:68081723 UT WOS 000387976803013 EID SCOPUS 85029900480 DOI 10.1016/j.prostr.2016.06.378 Anotace Nickel base superalloys exhibit fatigue fracture behavior with features of brittle-like cleavage cracking under high cycle fatigue loading at temperatures up to approximately 800 °C. This specific fracture behavior was already documented in several studies, but a possible mechanism of fatigue crack propagation under this mode has not been made completely clear yet. The aim of this paper is to put more light on the phenomenon by using advanced electron microscopy techniques like electron back-scattered diffraction (EBSD) and focused ion beam (FIB) sectioning. Fractured specimens after high cycle fatigue tests were thoroughly examined with the aim to localize the fatigue crack initiation sites and accompanying features of the fatigue crack propagation. Several specimens were cross-sectioned in order to characterize active slip systems, cyclic plastic deformation localization and fatigue crack propagation. Dislocation structures were studied by transmission electron microscopy (TEM). Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2017
Počet záznamů: 1