Ni-Au layers on sapphire prepared by direct current magnetron sputtering
- 1.0563460 - ÚJF 2023 RIV GB eng J - Článek v odborném periodiku
Mikšová, Romana - Jagerová, Adéla - Poustka, D. - Macková, Anna
Ni-Au layers on sapphire prepared by direct current magnetron sputtering.
Radiation Effects and Defects in Solids. Roč. 177, 11-12 (2022), s. 1288-1299. ISSN 1042-0150. E-ISSN 1029-4953
Grant CEP: GA MŠMT EF16_013/0001812
Výzkumná infrastruktura: CANAM II - 90056
Institucionální podpora: RVO:61389005
Klíčová slova: Bimetallic layer * SEM * magnetron sputtering * RBS
Obor OECD: Atomic, molecular and chemical physics (physics of atoms and molecules including collision, interaction with radiation, magnetic resonances, Mössbauer effect)
Impakt faktor: 1, rok: 2022
Způsob publikování: Omezený přístup
https://doi.org/10.1080/10420150.2022.2136091
Thin bimetallic Ni-Au layers (similar to 100 nm) with three different Au content were prepared by direct current magnetron sputtering onto sapphire substrates. The elemental composition and the layer thickness of bimetallic layers were controlled during the sputtering process. The prepared Ni-Au layers were annealed at temperatures of 400 degrees C and 900 degrees C in the air to determine the behavior of Au and Ni in the layers after heating. The elemental composition and depth profiling was provided by Rutherford backscattering spectrometry (RBS). The surface morphology was examined via Scanning electron microscopy (SEM). RBS measurement revealed inter-diffusion Au into sapphire substrate after thermal annealing and the formation of grains and voids.